Borealis PP HJ325MO
聚丙烯均聚物
Borealis AG
产品说明：
HJ325MO is a polypropylene homopolymer intended for injection moulding. Its very high melt flow makes it especially suitable for thin-wall packaging and products with long flow length. is designed for high-speed injection moulding and contains nucleating and antistatic additives. The additives are optimized to provide reduced tendency for mould plate-out.
This polymer is a CR (controlled rheology) grade with narrow molecular weight distribution giving low warpage. Components moulded from this grade show good ejectability and combine good stiffness with good transparency and gloss, good antistatic properties and good impact strength at ambient temperatures.
| 基本信息 | |
|---|---|
| 添加剂 |
|
| 特性 |
|
| 用途 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.910 | g/cm³ | ISO 1183 |
| 熔流率（熔体流动速率） (230°C/2.16 kg) | 50 | g/10 min | ISO 1133 |
| 收缩率 | 1.0 到 2.0 | % | 内部方法 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 洛氏硬度 (R 计秤) | 101 | ISO 2039-2 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | 1650 | MPa | ISO 527-2/1 |
| 拉伸应力 (屈服) | 35.0 | MPa | ISO 527-2/50 |
| 拉伸应变 (屈服) | 9.0 | % | ISO 527-2/50 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 (23°C) | 2.0 | kJ/m² | ISO 179/1eA |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 热变形温度 1(0.45 MPa, 未退火) | 103 | °C | ISO 75-2/B |
| *** | 额定值 | 单位制 | |
|---|---|---|---|
| 加工（熔体）温度 | 210 到 250 | °C | |
| 模具温度 | 10.0 到 30.0 | °C | |
| ***速度 | 快速 | ||
| 保压 | 20.0 到 50.0 | MPa |