Borealis PP BB125MO
聚丙烯共聚物
Borealis AG
产品说明：
BB125MO is a heterophasic copolymer. This grade is a low melt flow rate grade intended for blow moulding and sheet extrusion, and features extremely good processability with improved melt strength and melt stability. As all polypropylenes, this grade shows excellent stress-cracking and chemical resistances.
This polymer is one of the IMP (improved mechanical stability) grades, and is characterized by very high stiffness without any loss of impact strength even at low temperatures.
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.905 | g/cm³ | ISO 1183 |
| 熔流率（熔体流动速率） | ISO 1133 | ||
| 190°C/5.0 kg | 2.3 | g/10 min | ISO 1133 |
| 230°C/2.16 kg | 1.3 | g/10 min | ISO 1133 |
| 230°C/5.0 kg | 6.0 | g/10 min | ISO 1133 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | 1300 | MPa | ISO 527-2/50 |
| 拉伸应力 (屈服) | 25.0 | MPa | ISO 527-2/50 |
| 拉伸应变 (屈服) | 5.0 | % | ISO 527-2/50 |
| 弯曲模量 | 1200 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 简支梁缺口冲击强度 | ISO 179/1eA | ||
| -20°C | 7.0 | kJ/m² | ISO 179/1eA |
| 23°C | 50 | kJ/m² | ISO 179/1eA |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 热变形温度 (0.45 MPa, 未退火) | 85.0 | °C | ISO 75-2/B |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 料筒1区温度 | 190 到 220 | °C | |
| 料筒2区温度 | 190 到 220 | °C | |
| 料筒3区温度 | 190 到 220 | °C | |
| 料筒4区温度 | 190 到 220 | °C | |
| 料筒5区温度 | 190 到 220 | °C | |
| 熔体温度 | 180 到 220 | °C | |
| 口模温度 | 180 到 220 | °C |