RANPELEN SFC-750R
聚丙烯无规共聚物
Lotte Chemical Corporation
产品说明：
RANPELEN SFC-750R is a controlled medium modified polypropylene random copolymer designed for cast film technology. It offers an excellent clarity and gloss, a very low haze, a wide hot tack range, roll mark free and a low Heat seal temperature of 120°C. It is designed for quality packaging applicati***, as heat seal layer film. RANPELEN SFC-750R is easy processable on commercial cast film equipment. It contains slip and antiblock additives. RANPELEN SFC-750R is suitable for food contact.
| 基本信息 |
|
|---|
| 添加剂 | |
| 特性 | 低温热封性 高光 光滑性 抗结块性 清晰度，高 食品接触的合规性 无规共聚物
|
| 用途 | |
| 加工方法 | |
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 比重 | 0.900 | g/cm³ | ASTM D792, ISO 1183 |
| 熔流率（熔体流动速率） (230°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238, ISO 1133 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|
| 洛氏硬度 |
|
|
|
| R 级 | 82 |
| ASTM D785 |
| R 计秤 | 82 |
| ISO 2039-2 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 抗张强度 (屈服) | 22.6 | MPa | ASTM D638, ISO 527-2 |
| 伸长率 (断裂) | > 500 | % | ASTM D638, ISO 527-2 |
| 弯曲模量 | 785 | MPa | ASTM D790, ISO 178 |
| 摩擦系数 (铸造薄膜) | <1.0 |
| 内部方法 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 悬壁梁缺口冲击强度 (23°C) | 98 | J/m | ISO 180, ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 载荷下热变形温度 (0.45 MPa, 未退火) | 70.0 | °C | ASTM D648, ISO 75-2/B |
| 熔融温度 |
|
|
|
| -- | 131 | °C | 内部方法 |
| -- | 132 | °C | ASTM D3418 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 雾度 (30.0 µm, 铸造薄膜) | <2.0 | % | ASTM D1003 |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
|---|
| Heat Seal Temperature 1(30.0 µm) | 120 | °C | 内部方法 |