SEETEC PP R3450
聚丙烯无规共聚物
LG Chem Ltd.
产品说明：
Seetec R3450 is a polypropylene-ethylene random copolymer designed for the production of cast films. It has a good clarity due to the optimum content of ethylene and offers optimum balance between optical properties and physical strength. It is suitable for the skin layer of co-extruded cast film in food packaging or semi retort pouch being required high slip and medium heat seal temperature. SEETEC R3450 meets the FDA requirement in the code of Federal Regulati*** in 21 CFR 177.1520 and EU Directive 10/2011 for food contact.
| 基本信息 |
|
|---|
| 添加剂 | |
| 特性 | 高光滑性 高抗结块性 光学性能 可热封 良好的强度 清晰度，高 食品接触的合规性 通用
|
| 用途 | |
| 机构评级 | FDA 21 CFR 177.1520 欧洲 10/1/2011 12:00:00 AM
|
| 加工方法 | |
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 密度 | 0.900 | g/cm³ | ASTM D1505 |
| 熔流率（熔体流动速率） (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|
| 洛氏硬度 (R 级) | 82 |
| ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 抗张强度 1(屈服) | 25.0 | MPa | ASTM D638 |
| 伸长率 2(断裂) | > 500 | % | ASTM D638 |
| 弯曲模量 | 900 | MPa | ASTM D790 |
| 摩擦系数 (Static, 铸造薄膜) | <0.20 |
| ASTM D1894 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|
| 薄膜厚度 - 经测试 | 30 | µm |
|
| 抗张强度 |
|
| ASTM D882 |
| MD : 断裂, 30 µm, 挤塑薄膜 | 43.1 | MPa | ASTM D882 |
| TD : 断裂, 30 µm, 挤塑薄膜 | 33.3 | MPa | ASTM D882 |
| 伸长率 |
|
| ASTM D882 |
| MD : 断裂, 30 µm, 挤塑薄膜 | > 500 | % | ASTM D882 |
| TD : 断裂, 30 µm, 挤塑薄膜 | > 500 | % | ASTM D882 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 悬壁梁缺口冲击强度 (23°C) | 49 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 载荷下热变形温度 (0.45 MPa, 未退火) | 80.0 | °C | ASTM D648 |
| 维卡软化温度 | 134 | °C | ASTM D1525 3 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 光泽度 (30.0 µm, 铸造薄膜) | 132 |
| ASTM D2457 |
| 雾度 (30.0 µm, 铸造薄膜) | 1.5 | % | ASTM D1003 |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
|---|
| Heat Seal Temperature 4 | 130 | °C | 内部方法 |