1. 密炼室为“W"形，采用“M”形下加压盖，形成全封闭混炼空间。搅叶采用棱形螺旋无死角设计，使物料剪切分散达到物性要求。 W-shaped mixing chamber and M-shaped hammer to form a fully enclosed mixing space.The stirring blade is designed with a pri***atic helix no dead angle， so the material can be sheared and dispersed to meet the requirements.

2. 与物料接触部分（密炼室/侧板/压锤/搅叶轴）采用优质高碳钢，经调质、高精度机加工，真空72小时深度氮化热处理后表面喷涂碳化钨，后做光洁度处理 耐磨，防腐蚀，不易粘料，使用寿命长。 The contact part with material (mixing chamber/side plate/hammer/stirring blade shaft) is made of high quality high carbon teel， which is tempered and machined with high precision. After 72 hours of deep nitriding heat treatment in vacuum， the surface is sprayed with tungsten carbide，after finishing， it is wear-resistant，优质气氛保护密炼机， corrosion-resistant， non-ticky and longer service life.

密炼机操作方法

1、按照密炼炼室的容量和合适的填充系数（0.6～0.7），钛合金气氛保护密炼机，计算一次炼胶量和实际配方；

2、根据实际配方，准确称量配方中各种原材料的用量，将生胶、小料（ZnO、SA、促进剂、防老剂、 固体软化剂等）、补强剂或填充剂、液体软化剂、分别放置，在置物架上按顺序排好；

3、打开密炼机电源开关及加热开关，给密炼机预热，长海气氛保护密炼机，同时检查风压、水压、电压是否符合工艺要求，检查测温系统、计时装置、功率系统指示和记录是否正常；

4、密炼机预热好后，稳定一段时间，准备炼胶；

5、提起上顶栓，将已切成小块的生胶从加料口投入密炼机，落下上顶栓，炼胶1min；

6、提起上顶栓，加入小料，落下上顶栓混炼1.5min；

7、提起上顶栓，加入炭黑或填料，落下上顶栓混炼3min；

8、提起上顶栓，加入液体软化剂，落下上顶栓混炼1.5min；

9、排胶，用热电偶测胶料的温度，记录密炼室初始温度、混炼结束时密炼室温度及排胶温度，气氛保护钛合金密炼机，***大功率、转子的转速

正工机械设备厂是***研发.设计生产混炼机，开炼机，加压密炼式机，小型压片机的生产厂家。我们可以根据用户的不同需求设计

本机主要用于橡胶、塑胶及化工原料的混合密炼，也适用于各种高、低粘度物料的混炼。本机控温、分散均匀、简单实用，适合实验室的配方研发。

相关参数

1. 有效容量：1L

2. 温度范围：RT~260℃

3. 加热方式：电热管

4. 加热功率：2.4KW

5. 控 制 器：LED数字显示器，按键设定输入，数字显示输出

6. 硫化计时：LED数字显示器，0.1S~99M~9.9H密炼时间可以设置

7. 倒料方式：电机翻转倒料

8. 翻转角度：110°

9. 转子形状：M-W加压式与浇铸混合槽

10. 转子材质：38CrMoALA氮化 处理，硬度HRC60表面硬铬

11. 转子轴心深度：0.6-0.75MM，脆性不大于11级