Lexan PC 500ECR物性
|
10 ％玻璃纤维填充,注塑模压级,非氯化非溴化阻燃UL - 94 V0(2.3mm),它有各种不透明的颜色.
|
|
Property
|
| TYPICAL PROPERTIES (1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 5 mm/min
|
580
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Stress, brk, Type I, 5 mm/min
|
480
|
kgf/cm2
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 5 mm/min
|
4.7
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 5 mm/min
|
46
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 5 mm/min
|
25000
|
kgf/cm2
|
ASTM D 638
|
|
|
Flexural Stress, brk, 1.3 mm/min, 50 mm span
|
950
|
kgf/cm2
|
ASTM D 790
|
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
31800
|
kgf/cm2
|
ASTM D 790
|
|
|
Taber Abrasion, CS-17, 1 kg
|
11
|
mg/1000cy
|
SABIC Method
|
|
|
Tensile Stress, yield, 5 mm/min
|
60
|
MPa
|
ISO 527
|
|
|
Tensile Stress, break, 5 mm/min
|
45
|
MPa
|
ISO 527
|
|
|
Tensile Strain, yield, 5 mm/min
|
5
|
%
|
ISO 527
|
|
|
Tensile Strain, break, 5 mm/min
|
7
|
%
|
ISO 527
|
|
|
Tensile Modulus, 1 mm/min
|
3300
|
MPa
|
ISO 527
|
|
|
Flexural Stress, yield, 2 mm/min
|
95
|
MPa
|
ISO 178
|
|
|
Flexural Modulus, 2 mm/min
|
3400
|
MPa
|
ISO 178
|
|
|
Hardness, H358/30
|
115
|
MPa
|
ISO 2039-1
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, unnotched, 23°C, 6.4mm
|
NB
|
cm-kgf/cm
|
ASTM D 4812
|
|
|
Izod Impact, notched, 23°C
|
13
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched, -30°C
|
10
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Instrumented Impact Total Energy, 23°C
|
622
|
cm-kgf
|
ASTM D 3763
|
|
|
Izod Impact, unnotched 80*10*3 +23°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
|
Izod Impact, unnotched 80*10*3 -30°C
|
130
|
kJ/m2
|
ISO 180/1U
|
|
|
Izod Impact, notched 80*10*3 +23°C
|
10
|
kJ/m2
|
ISO 180/1A
|
|
|
Izod Impact, notched 80*10*3 -30°C
|
8
|
kJ/m2
|
ISO 180/1A
|
|
|
Izod Impact, unnotched 80*10*4 +23°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
|
Izod Impact, unnotched 80*10*4 -30°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
|
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm
|
10
|
kJ/m2
|
ISO 179/1eA
|
|
|
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm
|
9
|
kJ/m2
|
ISO 179/1eA
|
|
|
Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
|
Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
9
|
kJ/m2
|
ISO 179/1eA
|
|
|
Charpy Impact, notched, 23°C
|
15
|
kJ/m2
|
ISO 179/2C
|
|
|
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
|
Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
Vicat Softening Temp, Rate B/50
|
154
|
°C
|
ASTM D 1525
|
|
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
143
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
136
|
°C
|
ASTM D 648
|
|
|
CTE, -40°C to 40°C, flow
|
4.68E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, xflow
|
8.46E-05
|
1/°C
|
ASTM E 831
|
|
|
Thermal Conductivity
|
0.21
|
W/m-°C
|
ISO 8302
|
|
|
CTE, -40°C to 40°C, xflow
|
8.46E-05
|
1/°C
|
ISO 11359-2
|
|
|
CTE, 23°C to 80°C, flow
|
4.E-05
|
1/°C
|
ISO 11359-2
|
|
|
Ball Pressure Test, 125°C +/- 2°C
|
PASSES
|
-
|
IEC 60695-10-2
|
|
|
Vicat Softening Temp, Rate B/50
|
141
|
°C
|
ISO 306
|
|
|
Vicat Softening Temp, Rate B/120
|
143
|
°C
|
ISO 306
|
|
|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm
|
144
|
°C
|
ISO 75/Be
|
|
|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
|
136
|
°C
|
ISO 75/Ae
|
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
136
|
°C
|
ISO 75/Af
|
|
|
HDT/Ae, 1.8 MPa Annealed 120°C, 2hrs
|
142
|
°C
|
ISO 75/Ae
|
|
|
Relative Temp Index, Elec
|
130
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/impact
|
130
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/o impact
|
130
|
°C
|
UL 746B
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gravity
|
1.27
|
-
|
ASTM D 792
|
|
|
Mold Shrinkage, flow, 3.2 mm
|
0.4 - 0.6
|
%
|
SABIC Method
|
|
|
Mold Shrinkage, xflow, 3.2 mm
|
0.4 - 0.6
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 300°C/1.2 kgf
|
7.5
|
g/10 min
|
ASTM D 1238
|
|
|
Density
|
1.25
|
g/cm2
|
ISO 1183
|
|
|
Water Absorption, (23°C/sat)
|
0.31
|
%
|
ISO 62
|
|
|
Moisture Absorption (23°C / 50% RH)
|
0.13
|
%
|
ISO 62
|
|
|
Melt Volume Rate, MVR at 300°C/1.2 kg
|
7
|
cm210 min
|
ISO 1133
|
|
|
ELECTRICAL
|
Value | Unit | Standard | |
|
Hot Wire Ignition {PLC)
|
4
|
PLC Code
|
UL 746A
|
|
|
High Ampere Arc Ign, surface {PLC}
|
4
|
PLC Code
|
UL 746A
|
|
|
Comparative Tracking Index (UL) {PLC}
|
3
|
PLC Code
|
UL 746A
|
|
|
Volume Resistivity
|
>1.E+15
|
Ohm-cm
|
IEC 60093
|
|
|
Surface Resistivity, ROA
|
>1.E+15
|
Ohm
|
IEC 60093
|
|
|
Dielectric Strength, in oil, 0.8 mm
|
33
|
kV/mm
|
IEC 60243-1
|
|
|
Dielectric Strength, in oil, 1.6 mm
|
25
|
kV/mm
|
IEC 60243-1
|
|
|
Dielectric Strength, in oil, 3.2 mm
|
16
|
kV/mm
|
IEC 60243-1
|
|
|
Relative Permittivity, 50/60 Hz
|
2.9
|
-
|
IEC 60250
|
|
|
Relative Permittivity, 1 MHz
|
2.8
|
-
|
IEC 60250
|
|
|
Dissipation Factor, 50/60 Hz
|
0.001
|
-
|
IEC 60250
|
|
|
Dissipation Factor, 1 MHz
|
0.01
|
-
|
IEC 60250
|
|
|
Comparative Tracking Index
|
150
|
V
|
IEC 60112
|
|
|
FLAME CHARACTERISTICS
|
Value | Unit | Standard | |
|
UL Recognized, 94V-1 Flame Class Rating (3)
|
1.8
|
mm
|
UL 94
|
|
|
UL Recognized, 94V-0 Flame Class Rating (3)
|
2.3
|
mm
|
UL 94
|
|
|
Glow Wire Flammability Index 960°C, passes at
|
1
|
mm
|
IEC 60695-2-12
|
|
|
Glow Wire Ignitability Temperature, 1.0 mm
|
825
|
°C
|
IEC 60695-2-13
|
|
|
Oxygen Index (LOI)
|
36
|
%
|
ISO 4589
|
|
|
UV-light, water exposure/immersion
|
F2
|
-
|
UL 746C
|
|