| TYPICAL PROPERTIES(1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 5 mm/min
|
500
|
kgf/cm²
|
ASTM D 638
|
|
|
Tensile Modulus, 5 mm/min
|
24600
|
kgf/cm²
|
ASTM D 638
|
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
870
|
kgf/cm²
|
ASTM D 790
|
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
26700
|
kgf/cm²
|
ASTM D 790
|
|
|
Hardness, Rockwell R
|
113
|
-
|
ASTM D 785
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, notched, 23°C
|
16
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched, -40°C
|
3
|
cm-kgf/cm
|
ASTM D 256
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
107
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
95
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 6.4 mm, unannealed
|
101
|
°C
|
ASTM D 648
|
|
|
CTE, -40°C to 40°C, flow
|
6.66E-05
|
1/°C
|
ASTM E 831
|
|
|
Relative Temp Index, Elec
|
60
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/impact
|
60
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/o impact
|
60
|
°C
|
UL 746B
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gr***ity
|
1.05
|
-
|
ASTM D 792
|
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.5 - 0.8
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 230°C/3.8 kgf
|
1.5
|
g/10 min
|
ASTM D 1238
|
|
|
Melt Viscosity, 260°C, 1000 sec-1
|
2250
|
poise
|
ASTM D 3825
|
|
|
ELECTRICAL
|
Value | Unit | Standard | |
|
Arc Resistance, Tungsten {PLC}
|
6
|
PLC Code
|
ASTM D 495
|
|
|
Hot Wire Ignition {PLC)
|
4
|
PLC Code
|
UL 746A
|
|
|
High Voltage Arc Track Rate {PLC}
|
1
|
PLC Code
|
UL 746A
|
|
|
High Ampere Arc Ign, surface {PLC}
|
0
|
PLC Code
|
UL 746A
|
|
|
Comparative Tracking Index (UL) {PLC}
|
0
|
PLC Code
|
UL 746A
|
|
|
FLAME CHARACTERISTICS
|
Value | Unit | Standard | |
|
UL Recognized, 94HB Flame Class Rating (3)
|
1.47
|
mm
|
UL 94
|
|