| TYPICAL PROPERTIES(1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 50 mm/min
|
570
|
kgf/cm²
|
ASTM D 638
|
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
370
|
kgf/cm²
|
ASTM D 638
|
|
|
Tensile Stress, yld, Type I, 5 mm/min
|
520
|
kgf/cm²
|
ASTM D 638
|
|
|
Tensile Stress, brk, Type I, 5 mm/min
|
340
|
kgf/cm²
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
3
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
9
|
%
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 5 mm/min
|
2.8
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 5 mm/min
|
10
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 50 mm/min
|
27200
|
kgf/cm²
|
ASTM D 638
|
|
|
Tensile Modulus, 5 mm/min
|
27000
|
kgf/cm²
|
ASTM D 638
|
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
780
|
kgf/cm²
|
ASTM D 790
|
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
26500
|
kgf/cm²
|
ASTM D 790
|
|
|
Hardness, Shore D
|
78
|
-
|
ASTM D 2240
|
|
|
Tensile Stress, yield, 5 mm/min
|
50
|
MPa
|
ISO 527
|
|
|
Tensile Stress, break, 5 mm/min
|
35
|
MPa
|
ISO 527
|
|
|
Tensile Stress, yield, 50 mm/min
|
56
|
MPa
|
ISO 527
|
|
|
Tensile Stress, break, 50 mm/min
|
39
|
MPa
|
ISO 527
|
|
|
Tensile Strain, yield, 5 mm/min
|
2.8
|
%
|
ISO 527
|
|
|
Tensile Strain, break, 5 mm/min
|
10
|
%
|
ISO 527
|
|
|
Tensile Strain, yield, 50 mm/min
|
3
|
%
|
ISO 527
|
|
|
Tensile Strain, break, 50 mm/min
|
8
|
%
|
ISO 527
|
|
|
Tensile Modulus, 1 mm/min
|
2600
|
MPa
|
ISO 527
|
|
|
Flexural Stress, yield, 2 mm/min
|
80
|
MPa
|
ISO 178
|
|
|
Flexural Modulus, 2 mm/min
|
2700
|
MPa
|
ISO 178
|
|
|
Hardness, H358/30
|
100
|
MPa
|
ISO 2039-1
|
|
|
Hardness, Rockwell L
|
87
|
-
|
ISO 2039-2
|
|
|
Pencil Hardness test, 1kgf
|
HB
|
-
|
ASTM D 3363
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, notched, 23°C
|
8
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Izod Impact, notched, -30°C
|
6
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Multiaxial Impact
|
101
|
cm-kgf
|
ISO 6603
|
|
|
Instrumented Impact Total Energy, 23°C
|
254
|
cm-kgf
|
ASTM D 3763
|
|
|
Izod Impact, notched 80*10*4 +23°C
|
12
|
kJ/m²
|
ISO 180/1A
|
|
|
Izod Impact, notched 80*10*4 -30°C
|
7
|
kJ/m²
|
ISO 180/1A
|
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
13
|
kJ/m²
|
ISO 179/1eA
|
|
|
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm
|
8
|
kJ/m²
|
ISO 179/1eA
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
Vicat Softening Temp, Rate B/50
|
89
|
°C
|
ASTM D 1525
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
83
|
°C
|
ASTM D 648
|
|
|
CTE, -40°C to 40°C, flow
|
8.7E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, xflow
|
8.5E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, flow
|
8.7E-05
|
1/°C
|
ISO 11359-2
|
|
|
CTE, -40°C to 40°C, xflow
|
8.5E-05
|
1/°C
|
ISO 11359-2
|
|
|
Vicat Softening Temp, Rate A/50
|
98
|
°C
|
ISO 306
|
|
|
Vicat Softening Temp, Rate B/50
|
91
|
°C
|
ISO 306
|
|
|
Vicat Softening Temp, Rate B/120
|
92
|
°C
|
ISO 306
|
|
|
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
|
87
|
°C
|
ISO 75/Bf
|
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
77
|
°C
|
ISO 75/Af
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gr***ity
|
1.06
|
-
|
ASTM D 792
|
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.4 - 0.7
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 220°C/10.0 kgf
|
25
|
g/10 min
|
ASTM D 1238
|
|
|
Density
|
1.07
|
g/cm³
|
ISO 1183
|
|
|
Melt Volume Rate, MVR at 220°C/10.0 kg
|
25
|
cm³/10 min
|
ISO 1133
|
|
|
Melt Volume Rate, MVR at 260°C/5.0 kg
|
33
|
cm³/10 min
|
ISO 1133
|
|
|
FLAME CHARACTERISTICS
|
Value | Unit | Standard | |
|
UL Compliant, 94HB Flame Class Rating (3)(4)
|
1.5
|
mm
|
UL 94 by SABIC-IP
|
|