| TYPICAL PROPERTIES(1) | ||||
|
MECHANICAL
|
Value | Unit | Standard | |
|
Tensile Stress, yld, Type I, 5 mm/min
|
470
|
kgf/cm²
|
ASTM D 638
|
|
|
Tensile Stress, brk, Type I, 5 mm/min
|
360
|
kgf/cm²
|
ASTM D 638
|
|
|
Tensile Strain, yld, Type I, 5 mm/min
|
2
|
%
|
ASTM D 638
|
|
|
Tensile Strain, brk, Type I, 5 mm/min
|
18
|
%
|
ASTM D 638
|
|
|
Tensile Modulus, 5 mm/min
|
25300
|
kgf/cm²
|
ASTM D 638
|
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
800
|
kgf/cm²
|
ASTM D 790
|
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
26700
|
kgf/cm²
|
ASTM D 790
|
|
|
IMPACT
|
Value | Unit | Standard | |
|
Izod Impact, notched, 23°C
|
24
|
cm-kgf/cm
|
ASTM D 256
|
|
|
Instrumented Impact Total Energy, 23°C
|
214
|
cm-kgf
|
ASTM D 3763
|
|
|
THERMAL
|
Value | Unit | Standard | |
|
Vicat Softening Temp, Rate B/50
|
98
|
°C
|
ASTM D 1525
|
|
|
HDT, 0.45 MPa, 3.2 mm, unannealed
|
95
|
°C
|
ASTM D 648
|
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
82
|
°C
|
ASTM D 648
|
|
|
CTE, -40°C to 40°C, flow
|
8.82E-05
|
1/°C
|
ASTM E 831
|
|
|
CTE, -40°C to 40°C, xflow
|
8.46E-05
|
1/°C
|
ASTM E 831
|
|
|
Relative Temp Index, Elec
|
60
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/impact
|
60
|
°C
|
UL 746B
|
|
|
Relative Temp Index, Mech w/o impact
|
60
|
°C
|
UL 746B
|
|
|
PHYSICAL
|
Value | Unit | Standard | |
|
Specific Gr***ity
|
1.04
|
-
|
ASTM D 792
|
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.5 - 0.8
|
%
|
SABIC Method
|
|
|
Melt Flow Rate, 230°C/3.8 kgf
|
11.7
|
g/10 min
|
ASTM D 1238
|
|
|
Melt Viscosity, 240°C, 1000 sec-1
|
1720
|
poise
|
ASTM D 3825
|
|
|
Melt Flow Rate, 220°C/5.0 kg
|
12
|
g/10 min
|
ISO 1133
|
|
|
FLAME CHARACTERISTICS
|
Value | Unit | Standard | |
|
UL Recognized, 94HB Flame Class Rating (3)
|
1.52
|
mm
|
UL 94
|
|