Seamless pipe in nuclear power

· 用途：用于各种核反应堆的蒸汽发生器、燃料组件、堆内构件、驱动机构、换热器等一、二、三级用管和输送管道

· Usage：applied for pipe and transfer piping of all kinds of vapour generator， feul subassembly， in-pipe part and actuating mechani*** etc， in nuclear reactor.

· 订货标准Order norm：GB13296;GB/T14976;RCCM M4105;NB/T20008.7-2011;A***E SB163;agreement protocol etc

· 可供规格Offer specification：外径OD：8~325mm；壁厚WT：0.5~40mm

主要钢种（牌号）的化学成分和性能chemical composition and performance of main steel grade(trademark)

牌号trademark

原牌号（新牌号）化学成分chemical compositionNiCrFeMnCSiSPAlTiCu其它

othersWT%0Cr18Ni9

(06Cr19Ni10)8.0-

11.017.0-

19.0余bal≤2.0≤0.07≤1.00≤0.030≤0.035----00Cr19Ni10

(022Cr19Ni10)8.0-

12.018.0-

20.0余bal≤2.0≤0.030≤1.00≤0.030≤0.035----0Cr17Ni12Mo2

(06Cr17Ni12Mo2)11.0-

14.016.0-

18.5余bal≤2.0≤0.08≤1.00≤0.030≤0.035----00Cr17Ni14Mo2

(022Cr17Ni12Mo2)12.0-

15.016.0-

18.0余bal≤2.0≤0.03≤1.00≤0.030≤0.035----00Cr25Ni35AlTi34.0-

37.024.0-

26.5余bal0.5-

1.5≤0.0300.30-

0.70≤0.015≤0.0150.15- 0.450.15-

0.60≤0.50Co≤0.05

N≤0.03UNS N0880030.0-

35.019.0-

23.0≥39.5≤1.5≤0.10≤1.00≤0.015-0.15- 0.600.15-

0.60≤0.75-UNS N06600≥72.014.0-

17.06.0-

10.0≤1.0≤0.15≤0.50≤0.015---≤0.5-690

(NC30Fe)≥58.028.0-

31.08.0-

11.0≤0.50.01-

0.03≤0.50≤0.010≤0.015≤0.50≤0.50≤0.50Co≤0.018

Nb≤0.10

B≤0.003

N≤0.05690

(NS3105)≥58.028.0-

31.08.0-

11.0≤0.50.010-

0.03≤0.50≤0.010≤0.015≤0.50≤0.05≤0.05Nb≤0.10

B≤0.003

Co≤0.018

N≤0.05690(UNS NO6690)

A***E SB163及补充技术要求

A***E SB163 and additional technical requirements≥58.028.5-

31.09.0-

11.0≤0.50.015-

0.02≤0.50≤0.010≤0.015≤0.40≤0.35≤0.05Nb≤0.10

B≤0.002

Co≤0.016

N≤0.05

Mo≤0.2

· ASTM SB163 and additional technical requirements

· 690(NC30Fe/UNS N06690/NS3105)***力学性能及尺寸表面要求

技术指导

Standard690(NC30Fe)

RCCM M4105690(NS3105)

NB/T 20008.7-2001690(UNS NO6690)

A***E SB163及补充技术要求

A***E SB163 and additional technical requirements晶粒度

Grain size5-95-9，级差3级细于等于5级，级差小于2级

Less than ASTM5， not exceed two ASTM units室温拉伸

Room temperature tensileRm MPa≥630≥630gt;585Rp0.2 MPa275-375275-375275-380A%≥30≥30≥30350℃拉伸

350℃ tensileRm MPa≥533≥533≥550Rp0.2 MPa≥215≥215gt;215硬度 Hardness≤92≤92-扩口 flare-60°30%60°30%尺寸公差

Dimension tolerance外径OD mm19.05 /-0.0519.05 /-0.0517.48 /-0.05壁厚WT mm1.09 /-0.101.09 /-0.101.01 /-0.09长度L m19-2519-2519-29U形管椭圆度

U-bend tube ovality1-3排lt;5%1-3排≤5%1-5rowlt;2.8%4-6排lt;4%4-6排≤4%6-15rowlt;2.6%7-53排lt;3%7-53排≤3%16-164rowlt;1.6%内涡流性噪比

Noise levelgt;7单点single point≥7单点single point≥20水压试验

Hydrostatic14.7MPax10秒B级水

Demineralized water grade B14.7MPax10秒B级水

Demineralized water grade B21.42MPa≥5秒 ***水

Demineralized water grade A表面粗糙度

Surface roughness内Ralt;0.8、外Ralt;1.2

Inner surface Ralt;0.8

Outer surface Ralt;1.2内Ra≤0.8、外Ra≤1.2

Inner surface Ra≤0.8

Outer surface Ra≤1.2内Ralt;0.5、外Ralt;1.0

Inner surface Ralt;0.5

Outer surface Ralt;1.0晶间腐蚀

Intergranular corrosion--≤20mdd

　1、钢材按品质分类

　　(1) 普通钢(P≤0.045%，S≤0.050%)

　　(2) 优钢材质钢(P、S均≤0.035%)

　　(3) 优质钢(P≤0.035%，S≤0.030%)

　　2.、按化学成份分类

　　(1) 碳素钢：钢材a.低碳钢(C≤0.25%);b.中碳钢(C≤0.25~0.60%);c.高碳钢(C≤0.60%)。

　　(2) 合金钢：a.低合金钢(合金元素总含量≤5%);b.中合金钢(合金元素总含量gt;5~10%);c.高合金钢(合金元素总含量gt;10%)。

　　3、钢材按成形方法分类：(1) 锻钢;(2) 铸钢;(3) 热轧钢;(4) 冷拉钢。

1.壁厚不均

　　钢管壁厚不可能各处相同，在其横截面及纵向管体上客观存在壁厚不等现象，即壁厚不均。为了控制这种不均匀性，在有的钢管标准中规定了壁厚不均的允许指标，一般规定不超过壁厚公差的80%(经供需双方协商后执行)。

　　2.椭圆度

　　在圆形钢管的横截面上存在着外径不等的现象，即存在着不一定互相垂直的外径和外径，则外径与外径之差即为椭圆度(或不圆度)。为了控制椭圆度，有的钢管标准中规定了椭圆度的允许指标，一般规定为不超过外径公差的80%(经供需双方协商后执行)。

　　3.弯曲度

　　钢管在长度方向上呈曲线状，用数字表示出其曲线度即叫弯曲度。标准中规定的弯曲度一般分为如下两种：

　　A、局部弯曲度：用一米长直尺靠量在钢管的弯曲处，测其弦高(mm)，即为局部弯曲度数值，其单位为mm/m，表示方法如2.5mm/m。此种方法也适用于管端部弯曲度。

　　B、全长总弯曲度：用一根细绳，从管的两端拉紧，无缝管，测量钢管弯曲处弦高(mm)，然后换算成长度(以米计)的百分数，即为钢管长度方向的全长弯曲度。

　　例如：钢管长度为8m，测得弦高30mm，则该管全长弯曲度应为：

　　0.03÷8m×100%=0.375%

　　4.尺寸超差

　　尺寸超差或叫尺寸超出标准的允许偏差。此处的"尺寸"主要指钢管的外径和壁厚。通常有人把尺寸超差习惯叫"公差出格"，这种把偏差和公差等同起来的叫法是不严密的，应叫"偏差出格"。此处的偏差可能是"正"的，也可能是"负"的，很少在同一批钢管中出现"正、负"偏差均出格的现象。