PC 104R物性
TYPICAL PROPERTIES (1) | ||||
MECHANICAL
|
Value | Unit | Standard | |
Tensile Stress, yld, Type I, 50 mm/min
|
630
|
kgf/cm²
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
690
|
kgf/cm²
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
7
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
135
|
%
|
ASTM D 638
|
|
Tensile Modulus, 5 mm/min
|
23500
|
kgf/cm²
|
ASTM D 638
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
980
|
kgf/cm²
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
23800
|
kgf/cm²
|
ASTM D 790
|
|
Hardness, Rockwell M
|
70
|
-
|
ASTM D 785
|
|
Hardness, Rockwell R
|
118
|
-
|
ASTM D 785
|
|
Taber Abrasion, CS-17, 1 kg
|
10
|
mg/1000cy
|
ASTM D 1044
|
|
Taber Abrasion, CS-17, 1 kg
|
10
|
mg/1000cy
|
SABIC Method
|
|
Tensile Stress, yield, 50 mm/min
|
63
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 50 mm/min
|
70
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 50 mm/min
|
6
|
%
|
ISO 527
|
|
Tensile Strain, break, 50 mm/min
|
120
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min
|
2350
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min
|
90
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min
|
2300
|
MPa
|
ISO 178
|
|
Hardness, H358/30
|
95
|
MPa
|
ISO 2039-1
|
|
IMPACT
|
Value | Unit | Standard | |
Izod Impact, unnotched, 23°C
|
326
|
cm-kgf/cm
|
ASTM D 4812
|
|
Izod Impact, notched, 23°C
|
92
|
cm-kgf/cm
|
ASTM D 256
|
|
Izod Impact, notched, -30°C
|
14
|
cm-kgf/cm
|
ASTM D 256
|
|
Tensile Impact, Type S
|
642
|
cm-kgf/cm²
|
ASTM D 1822
|
|
Falling Dart Impact (D 3029), 23°C
|
1723
|
cm-kgf
|
ASTM D 3029
|
|
Instrumented Impact Total Energy, 23°C
|
662
|
cm-kgf
|
ASTM D 3763
|
|
Izod Impact, notched 80*10*4 +23°C
|
65
|
kJ/m²
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*4 -30°C
|
10
|
kJ/m²
|
ISO 180/1A
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
95
|
kJ/m²
|
ISO 179/1eA
|
|
Charpy Impact, notched, 23°C
|
35
|
kJ/m²
|
ISO 179/2C
|
|
THERMAL
|
Value | Unit | Standard | |
Vicat Softening Temp, Rate B/50
|
154
|
°C
|
ASTM D 1525
|
|
HDT, 0.45 MPa, 6.4 mm, unannealed
|
137
|
°C
|
ASTM D 648
|
|
HDT, 1.82 MPa, 6.4 mm, unannealed
|
132
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 40°C, flow
|
6.2E-05
|
1/°C
|
ASTM E 831
|
|
CTE, -40°C to 40°C, xflow
|
5.7E-05
|
1/°C
|
ASTM E 831
|
|
Specific Heat
|
1.25
|
J/g-°C
|
ASTM C 351
|
|
Thermal Conductivity
|
0.19
|
W/m-°C
|
ASTM C 177
|
|
Thermal Conductivity
|
0.2
|
W/m-°C
|
ISO 8302
|
|
CTE, -40°C to 40°C, flow
|
6.E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, -40°C to 40°C, xflow
|
6.E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, 23°C to 80°C, flow
|
7.E-05
|
1/°C
|
ISO 11359-2
|
|
Ball Pressure Test, 125°C +/- 2°C
|
PASSES
|
-
|
IEC 60695-10-2
|
|
Ball Pressure Test, approximate maximum
|
140
|
°C
|
IEC 60695-10-2
|
|
Vicat Softening Temp, Rate B/50
|
144
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120
|
145
|
°C
|
ISO 306
|
|
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm
|
138
|
°C
|
ISO 75/Be
|
|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
|
127
|
°C
|
ISO 75/Ae
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
124
|
°C
|
ISO 75/Af
|
|
Relative Temp Index, Elec
|
130
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact
|
130
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact
|
130
|
°C
|
UL 746B
|
|
PHYSICAL
|
Value | Unit | Standard | |
Specific Gravity
|
1.2
|
-
|
ASTM D 792
|
|
Specific Volume
|
0.83
|
cm³/g
|
ASTM D 792
|
|
Density
|
1.19
|
g/cm³
|
ASTM D 792
|
|
Water Absorption, 24 hours
|
0.15
|
%
|
ASTM D 570
|
|
Water Absorption, equilibrium, 23C
|
0.35
|
%
|
ASTM D 570
|
|
Water Absorption, equilibrium, 100°C
|
0.58
|
%
|
ASTM D 570
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.5 - 0.7
|
%
|
SABIC Method
|
|
Melt Flow Rate, 300°C/1.2 kgf
|
7
|
g/10 min
|
ASTM D 1238
|
|
Density
|
1.2
|
g/cm³
|
ISO 1183
|
|
Water Absorption, (23°C/sat)
|
0.35
|
%
|
ISO 62
|
|
Moisture Absorption (23°C / 50% RH)
|
0.15
|
%
|
ISO 62
|
|
Melt Volume Rate, MVR at 220°C/5.0 kg
|
4
|
cm³/10 min
|
ISO 1133
|
|
Melt Volume Rate, MVR at 300°C/1.2 kg
|
6
|
cm³/10 min
|
ISO 1133
|
|
OPTICAL
|
Value | Unit | Standard | |
Light Transmission, 2.54 mm
|
88
|
%
|
ASTM D 1003
|
|
Haze, 2.54 mm
|
1
|
%
|
ASTM D 1003
|
|
Refractive Index
|
1.586
|
-
|
ASTM D 542
|
|
Refractive Index
|
1.586
|
-
|
ISO 489
|
|
ELECTRICAL
|
Value | Unit | Standard | |
Volume Resistivity
|
>1.E+17
|
Ohm-cm
|
ASTM D 257
|
|
Dielectric Strength, in air, 3.2 mm
|
14.9
|
kV/mm
|
ASTM D 149
|
|
Relative Permittivity, 50/60 Hz
|
3.17
|
-
|
ASTM D 150
|
|
Relative Permittivity, 1 MHz
|
2.96
|
-
|
ASTM D 150
|
|
Dissipation Factor, 50/60 Hz
|
0.0009
|
-
|
ASTM D 150
|
|
Dissipation Factor, 1 MHz
|
0.01
|
-
|
ASTM D 150
|
|
Hot Wire Ignition {PLC)
|
2
|
PLC Code
|
UL 746A
|
|
High Voltage Arc Track Rate {PLC}
|
2
|
PLC Code
|
UL 746A
|
|
High Ampere Arc Ign, surface {PLC}
|
1
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index (UL) {PLC}
|
2
|
PLC Code
|
UL 746A
|
|
Dielectric Strength, in oil, 3.2 mm
|
17
|
kV/mm
|
IEC 60243-1
|
|
Relative Permittivity, 1 MHz
|
2.7
|
-
|
IEC 60250
|
|
Dissipation Factor, 50/60 Hz
|
0.001
|
-
|
IEC 60250
|
|
Dissipation Factor, 1 MHz
|
0.01
|
-
|
IEC 60250
|
|
Relative Permittivity, 50/60 Hz
|
2.7
|
-
|
IEC 60250
|
|
FLAME CHARACTERISTICS
|
Value | Unit | Standard | |
UL Recognized, 94HB Flame Class Rating (3)
|
1.47
|
mm
|
UL 94
|
|
Glow Wire Flammability Index 850°C, passes at
|
1
|
mm
|
IEC 60695-2-12
|
|
Oxygen Index (LOI)
|
25
|
%
|
ISO 4589
|
Source GMD, last updated:2006/12/01
|
Processing
|
Parameter | ||
Injection Molding
|
Value | Unit |
Drying Temperature
|
120
|
°C
|
Drying Time
|
3 - 4
|
hrs
|
Drying Time (Cumulative)
|
48
|
hrs
|
Maximum Moisture Content
|
0.02
|
%
|
Melt Temperature
|
310 - 330
|
°C
|
Nozzle Temperature
|
305 - 325
|
°C
|
Front - Zone 3 Temperature
|
310 - 330
|
°C
|
Middle - Zone 2 Temperature
|
300 - 320
|
°C
|
Rear - Zone 1 Temperature
|
290 - 310
|
°C
|
Mold Temperature
|
80 - 115
|
°C
|
Back Pressure
|
0.3 - 0.7
|
MPa
|
Screw Speed
|
40 - 70
|
rpm
|
Shot to Cylinder Size
|
40 - 60
|
%
|
Vent Depth
|
0.025 - 0.076
|
mm
|