产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 熔体流动速率 | 240℃/10.0kg | ISO 1133 | 23 | g/10min |
| 比重 | ASTM D-7921.18g/cm3 | |||
| ISO 1183 | ||||
| 模具收缩率 | 流动 | ASTM D-955 | 0.1-0.3 | % |
| 拉伸模量 | ISO 527-2/17300MPa | |||
| 抗张屈服强度 | ASTM D-638110MPa | |||
| ISO 527-2/5095.0 | ||||
| 断裂伸长率 | ASTM D-6383.0% | |||
| ISO 527-2/502.0 | ||||
| 弯曲模量 | ASTM D-7906050MPa | |||
| 弯曲屈服强度 | ASTM D-790150MPa | |||
| ISO 178156 | ||||
| 简支梁缺口冲击强度 | 23℃ | ISO 179/1eA | 7.0 | KJ/m2 |
| 悬壁梁缺口冲击强度 | 23℃,12.7mm | ASTM D-256 | 80.0 | J/m |
| 洛氏硬度 | ASTM D-785121R-scale | |||
| 热变形温度 | 1.80MPa，未退火，6.40mm | ASTM D-648 | 106 | ℃ |
| 1.80MPa，未退火ISO 75-2/A101 | ||||
| 阻燃等级 | UL94HB |