POM/(聚甲醛#赛钢)/***0-04/日本宝理
用途： 电子电器,家用电器
材料特性：共聚甲醛
重要参数： 密度:1.41 g/cm3 吸水率:0.22 % 缺口冲击强度:63 拉伸强度:60 MPa 弯曲强度:96 MPa 弯曲模量:2580 MPa 硬度:80 热变形温度:110 ℃
生产厂商：日本宝理
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |||||||||
| 基本性能 | 吸水率 | 23℃，24hr | ASTM D-570 | 0.22 | % | ||||||||
| 物理性能 |
|
--- |
|
|
--- | ||||||||
| 比重 | --- | ASTM D-792 | 1.41 | --- | |||||||||
| 机械性能 | 抗拉强度 | --- | ASTM D-638 | 60 | MPa | ||||||||
| 拉伸率 | --- | ASTM D-638 | 60 | % | |||||||||
| 弯曲强度 | --- | ASTM D-790 | 96 | MPa | |||||||||
| 弯曲模量 | --- | ASTM D-790 | 2580 | MPa | |||||||||
|
--- |
|
|
|
|||||||||
| 洛氏硬度 | --- | ASTM D-785 | 80 | M | |||||||||
| 电气性能 | 体积电阻系数 | --- | ASTM D-257 | 1×1014 | Ω.cm | ||||||||
| 表面电阻系数 | --- | ASTM D-257 | 1×1016 | Ω | |||||||||
| 介***穿强度 | --- | ASTM D-149 | 24 | MV/m | |||||||||
| 热 性 能 | 负荷挠曲温度 | 1.32MPa | ASTM D-648 | 110 | ℃ | ||||||||
| 线膨胀系数 | --- | ASTM D-596 | 10 | ×10-5/℃ | |||||||||
| 燃烧性 | --- | UL 94 | 94HB | --- | |||||||||