物理性能
|
种类的记号
|
调质记号
|
冷轧、固溶化热处理或退火状态
|
析出硬化热处理状态
|
导电%
|
||||||
|
硬度HV
|
屈服强度N/mm
|
抗拉强度N/mm
|
伸长%
|
热处理记号
|
硬度HV
|
屈服强度N/mm
|
抗拉强度N/mm
|
|||
|
301-CSP
|
1/2H
|
340&plu***n;30
|
≥510
|
≥930
|
≥10
|
-
|
-
|
-
|
-
|
2.3
|
|
3/4H
|
400&plu***n;30
|
≥745
|
≥1130
|
≥5
|
-
|
-
|
-
|
-
|
2.3
|
|
|
H
|
460&plu***n;30
|
≥1030
|
≥1320
|
-
|
-
|
-
|
-
|
-
|
2.3
|
|
|
EH
|
510&plu***n;20
|
≥1275
|
≥1570
|
-
|
-
|
-
|
-
|
-
|
2.3
|
|
|
SEH
|
≥530
|
≥1450
|
≥1740
|
-
|
-
|
-
|
-
|
-
|
2.3
|
|
|
304-CSP
|
1/2H
|
280&plu***n;30
|
≥470
|
≥780
|
≥6
|
-
|
-
|
-
|
-
|
2.3
|
|
3/4H
|
340&plu***n;30
|
≥665
|
≥930
|
≥3
|
-
|
-
|
-
|
-
|
2.3
|
|
|
H
|
≥370
|
≥880
|
≥1130
|
-
|
-
|
-
|
-
|
-
|
2.3
|
|
|
631-CSP
|
0
|
≤200
|
-
|
≤1030
|
≥20
|
TH1050RH950
|
≥345≥392
|
≥960≥1030
|
≥1140≥1230
|
2.3
|
|
1/2H
|
375&plu***n;25
|
-
|
≥1080
|
≥5
|
CH
|
≥380
|
≥880
|
≥1230
|
2.3
|
|
|
3/4H
|
425&plu***n;25
|
-
|
≥1180
|
CH
|
≥450
|
≥1080
|
≥1420
|
2.3
|
||
|
H
|
≥450
|
-
|
≥1420
|
CH
|
≥530
|
≥1320
|
≥1720
|
2.3
|
||
1.屈服强度（σ0.2）：使产生***残余塑性变形等于一定值（一般为原长度的0.2%）时的应力，称为屈服强度σ0.2。
2.抗拉强度（σb）：材料在拉伸过程中，从开始到发生断裂时所达到的***大应力值。它表示钢材抵抗断裂的能力大小。设Pb为材料被拉断前达到的***大拉力，Fo为试样截面面积，则抗拉强度σb= Pb/Fo （MPa）。
3.伸长率（δs）：材料在拉断后，其塑性伸长的长度与原试样长度的百分比叫伸长率或延伸率。
4.硬度：硬度表示材料抵抗硬物体压入其表面的能力。它是金属材料的重要性能指标之一。一般硬度越高，耐磨性越好。
化学成分
品名：宝钢304不锈钢带，304不锈钢带材，304不锈钢卷带、316不锈钢卷带、301不锈钢卷带，
化学成分
C≤0.08
Si≤1.00
Mn≤2.00
P≤0.035
S≤0.03
Ni:8.0-10.0
Cr:18.0-20.0
性质
拉强度(Mpa) 620 MIN
屈服强度(Mpa) 310 MIN
伸长率(%) 30 MIN
面积缩减(%) 40 MIN
304不锈钢的密度 7.93 g/cm3
奥氏体不锈钢一般都用这个值
304含铬量(%) 18--20 .
304相当于我国的0Cr19Ni9 (0Cr18Ni9)不锈钢