PPS(聚苯硫醚#)/A504-02/日本东丽
用途： 其它
重要参数： 密度:1.7 g/cm3 吸水率:0.02 % 成型收缩率:0.7 % 缺口冲击强度:100 拉伸强度:140 MPa 弯曲强度:200 MPa 硬度:122 热变形温度:260 ℃
生产厂商：日本东丽
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |||||||||
| 基本性能 | 吸水率 | --- | ASTM D-570 | 0.02 | % | ||||||||
| 物理性能 | 比重 | --- | ASTM D-792 | 1.70 | --- | ||||||||
|
--- |
|
|
|
|||||||||
| 流动长 | 320℃,98MPa,1mm厚 | 东丽法 | 155 | ×10-3m | |||||||||
| 机械性能 | 引张强度 | --- | ASTM D-638 | 140 | MPa | ||||||||
| 拉伸强度 | --- | ASTM D-638 | 1.5 | % | |||||||||
| 弯曲强度 | --- | ASTM D-790 | 200 | MPa | |||||||||
| 弯曲弹性体 | --- | ASTM D-790 | 14.7 | GPa | |||||||||
| 断裂强度 | --- | ASTM D-732 | 75 | --- | |||||||||
|
--- |
|
|
|
|||||||||
| 硬度 | --- | ASTM D-785 | 122 | 洛氏 | |||||||||
| 摩耗 | --- | ASTM D-1044 | 50 | mg/1000回 | |||||||||
| 摩擦系数 | 对钢 | ASTM D-1894 | 0.25 | --- | |||||||||
| 限界PV值 | --- | 东丽法 | 815 | kj/m2.hr | |||||||||
| 电气性能 | 耐电弧性W电级 | --- | ASTM D-495 | 127 | 秒 | ||||||||
| 体积固有抵抗 | --- | ASTM D-257 | 1016 | Ω.m | |||||||||
| 绝缘***电压 | --- | ASTM D-149 | 21 | MV/m | |||||||||
| 诱电率 | 106Hz | ASTM D-150 | 3.8 | --- | |||||||||
| 诱电正接 | 106Hz | ASTM D-150 | 0.002 | --- | |||||||||
| 热 性 能 | 融点 | --- | DSC | 278 | ℃ | ||||||||
| 热变形温度 | 1.82MPa | ASTM D-648 | >260 | ℃ | |||||||||
|
--- |
|
|
|
|||||||||
| 燃烧性 | --- | UL-94 | V-0 | --- | |||||||||