现货A5052P-O铝板料 进口JIS标准
Aluminum 5052-H34
Subcategory: 5000 Series Aluminum Alloy; Aluminum Alloy; Metal; Nonferrous Metal
Close Analogs:
Composition Notes:
Aluminum content reported is calculated as remainder.
Composition information provided by the Aluminum Association and is not for design.
Key Wo***: UNS A95052; ISO AlMg2.5; Aluminium 5052-H34; AA5052-H34
|
|
|
Material Notes:
Data points with the AA note h***e been provided by the Aluminum Association, Inc. and are NOT FOR DESIGN.
Physical Properties | Metric | English | Comments | |
|
||||
Density | 2.68 g/cc | 0.0968 lb/in� | AA; Typical | |
Mechanical Properties |
||||
|
||||
Hardness, Brinell | 68 | 68 | AA; Typical; 500 g load; 10 mm ball | |
Hardness, Knoop | 91 | 91 | Converted from Brinell Hardness Value | |
Hardness, Vickers | 78 | 78 | Converted from Brinell Hardness Value | |
Ultimate Tensile Strength | 262 MPa | 38000 psi | AA; Typical | |
Tensile Yield Strength | 214 MPa | 31000 psi | AA; Typical | |
Elongation at Break | 10 % | 10 % | AA; Typical; 1/16 in. (1.6 mm) Thickness | |
Elongation at Break | 14 % | 14 % | AA; Typical; 1/2 in. (12.7 mm) Diameter | |
Modulus of Elasticity | 70.3 GPa | 10200 ksi | AA; Typical; ***erage of tension and compression. Compression modulus is about 2% greater than tensile modulus. | |
Ultimate Bearing Strength | 469 MPa | 68000 psi | Edge distance/pin diameter = 2.0 | |
Bearing Yield Strength | 303 MPa | 43900 psi | Edge distance/pin diameter = 2.0 | |
Poisson's Ratio | 0.33 | 0.33 | ||
Fatigue Strength | 124 MPa | 18000 psi | AA; 500,000,000 cycles completely reversed stress; RR Moore machine/specimen | |
Machinability | 50 % | 50 % | 0-100 Scale of Aluminum Alloys | |
Shear Modulus | 25.9 GPa | 3760 ksi | ||
Shear Strength | 145 MPa | 21000 psi | AA; Typical | |
Electrical Properties |
||||
|
||||
Electrical Resistivity | 4.99e-006 ohm-cm | 4.99e-006 ohm-cm | AA; Typical at 68癋 | |
Thermal Properties |
||||
|
||||
CTE, linear 68癋 | 23.8 祄/m-癈 | 13.2 礽n/in-癋 | AA; Typical; ***erage over 68-212癋 range. | |
CTE, linear 250癈 | 25.7 祄/m-癈 | 14.3 礽n/in-癋 | ***erage over the range 20-300篊 | |
Specific Heat Capacity | 0.88 J/g-癈 | 0.21 BTU/lb-癋 | Estimated from trends in similar Al alloys. | |
Thermal Conductivity | 138 W/m-K | 960 BTU-in/hr-ft�-癋 | AA; Typical at 77癋 | |
Melting Point | 607 - 649 癈 | 1125 - 1200 癋 | AA; Typical range based on typical composition for wrought products 1/4 inch thickness or greater | |
Solidus | 607 癈 | 1125 癋 | AA; Typical | |
Liquidus | 649 癈 | 1200 癋 | AA; Typical | |
Processing Properties |
||||
|
||||
Annealing Temperature | 343 癈 | 650 癋 | holding at temperature not required | |
Hot-Working Temperature | 260 - 510 癈 | 500 - 950 癋 |