美国首诺 21S***A66
美国首诺 21S***A66收缩率
| 收缩率 | AcrossFlow:23°C,2.00mm | ISO294-4 | 1.7 | % | |
| Flow:23°C,2.00mm | ISO294-4 | 1.8 | % | ||
| 吸水率(23°C,24hr) | ISO62 | 1.2 | % | ||
| 吸水率(平衡,23°C,50%RH) | ISO62 | 2.4 | % | ||
| 室外适用性 | UL746C | f2 | |||
| 机械性能 | 拉伸模量(23°C) | ISO527-2 | 3100 | MPa | |
| 拉伸应力(屈服,23°C) | ISO527-2 | 82.0 | MPa | ||
| 拉伸应力(断裂,23°C) | ISO527-2 | 55.0 | MPa | ||
| 拉伸应变(屈服,23°C) | ISO527-2 | 5.0 | % | ||
| 标称拉伸断裂应变(23°C) | ISO527-2 | 25 | % | ||
| 弯曲模量(23°C) | ISO178 | 2900 | MPa | ||
| 弯曲强度(23°C) | ISO178 | 80.0 | MPa | ||
| 泊松比 | ISO527 | 0.40 | |||
| 冲击性能 | 简支梁缺口冲击强度 | -30°C | ISO179/1eA | 5.0 | kJ/m² |
| 23°C | ISO179/1eA | 6.0 | kJ/m² | ||
| 简支梁无缺口冲击强度 | -30°C | ISO179/1eU | NoBreak | ||
| 23°C | ISO179/1eU | NoBreak | |||
| 悬壁梁缺口冲击强度 | -30°C | ISO180 | 5.0 | kJ/m² | |
| 23°C | ISO180 | 6.0 | kJ/m² | ||
| 热性能 | 热变形温度(0.45MPa,未退火) | ISO75-2/B | 200 | °C | |
| 热变形温度(1.8MPa,未退火) | ISO75-2/A | 70.0 | °C | ||
| 熔融温度 | ISO11357-3 | 260 | °C | ||
| 线形热膨胀系数-流动(23到55°C) | ISO11359-2 | 1.0E-4 | cm/cm/°C | ||
| CLTE-Transverse(23to55°C) | ISO11359-2 | 1.0E-4 | cm/cm/°C | ||
| RTIElec | 0.71mm | UL746 | 130 | °C | |
| 1.5mm | UL746 | 130 | °C | ||
| 3.0mm | UL746 | 130 | °C | ||
| RTIImp | 0.71mm | UL746 | 75.0 | °C | |
| 1.5mm | UL746 | 75.0 | °C | ||
| 3.0mm | UL746 | 75.0 | °C | ||
| RTIStr | 0.71mm | UL746 | 85.0 | °C | |
| 1.5mm | UL746 | 85.0 | °C | ||
| 3.0mm | UL746 | 85.0 | °C | ||
| 电气性能 | VolumeResistivity(0.750mm) | IEC60093 | 1.0E+13 | ohms·cm | |
| 介电强度(1.00mm) | IEC60243 | 26 | kV/mm | ||
| 耐电弧性(3.00mm) | ASTMD495 | PLC5 | |||
| 漏电起痕指数(3.00mm) | IEC60112 | 600 | V | ||
| 高电弧燃烧指数(HAI) | 0.71mm | UL746 | PLC0 | ||
| 1.5mm | UL746 | PLC0 | |||
| 3.0mm | UL746 | PLC0 | |||
| 高电压电弧起痕速率(HVTR) | UL746 | PLC0 | |||
| 热丝引燃(HWI) | 0.71mm | UL746 | PL*** | ||
| 1.5mm | UL746 | PLC3 | |||
| 3.0mm | UL746 | PLC2 | |||
| 可燃性 | UL阻燃等级 | 0.71mm | UL94 | V-2 | |
| 1.5mm | UL94 | V-2 | |||
| 3.0mm | UL94 | V-2 | |||
| 灼热丝***指数 | 0.71mm | IEC60695-2-12 | 960 | °C | |
| 1.5mm | IEC60695-2-12 | 960 | °C | ||
| 3.0mm | IEC60695-2-12 | 960 | °C | ||
| 热灯丝点火温度 | 0.71mm | IEC60695-2-13 | 850 | °C | |
| 1.5mm | IEC60695-2-13 | 850 | °C | ||
| 3.0mm | IEC60695-2-13 | 850 | °C | ||
| 极限氧指数 | ISO4589-2 | 25 | % |