吸水率美国杜邦101LPA66
101L
| 吸水率 | 24小时浸渍(23℃) | ASTM D-570 | DAM｜1.2 | % | |
| 24小时浸渍(23℃) | ASTM D-570 | 50%RH｜- | % | ||
| 饱和(23℃) | ASTM D-570 | DAM｜8.5 | % | ||
| 饱和(23℃) | 50%RH｜- | % | |||
| 物理性能 | 比重 | ASTM D-792 | DAM｜1.14 | ||
| ASTM D-792 | 50%RH｜1.14 | ||||
| 泰伯磨耗量 | cs-17 Wheel,1000g | DAM｜- | mg/1000 cycles | ||
| cs-17 Wheel,1000g | 50%RH｜7 | mg/1000 cycles | |||
| 机械性能 | 埃佐冲击强度 | 23℃ | ASTM D-256 | DAM｜53 | j/m |
| 23℃ | ASTM D-256 | 50%RH｜112 | j/m | ||
| 洛氏硬度M | ASTM D-785 | DAM｜M79 | |||
| ASTM D-785 | 50%RH｜M59 | ||||
| 硬度计硬度 | ASTM D-676 | DAM｜89 | |||
| ASTM D-676 | 50%RH｜82 | ||||
| 洛氏硬度R | ASTM D-785 | DAM｜R121 | |||
| ASTM D-785 | 50%RH｜R108 | ||||
| 屈服强度 | 23℃ | DAM｜82.7 | MPa | ||
| 23℃ | 50%RH｜58.6 | MPa | |||
| 拉伸强度 | 23℃ | ASTM D-638 | DAM｜82.7 | MPa | |
| 23℃ | ASTM D-638 | 50%RH｜77.2 | MPa | ||
| 揉曲模量 | 23℃ | ASTM D-790 | DAM｜2827 | MPa | |
| 23℃ | ASTM D-790 | 50%RH｜1207 | MPa | ||
| 拉伸冲击强度 | 短试样23℃ | ASTM D-1822 | DAM｜157 | KJ/m2 | |
| 短试样23℃ | ASTM D-1822 | 50%RH｜231 | KJ/m2 | ||
| 1%形变时的压应力 | ASTM D-695 | DAM｜33.8 | MPa | ||
| ASTM D-695 | 50%RH｜- | MPa | |||
| 剪切强度 | 23℃ | ASTM D-732 | DAM｜66.2 | MPa | |
| 23℃ | ASTM D-732 | 50%RH｜- | MPa | ||
| 断裂伸长率 | 23℃ | ASTM D-638 | DAM｜60 | % | |
| 23℃ | ASTM D-638 | 50%RH｜≥300 | % | ||
| 屈服伸长率 | ASTM D-638 | DAM｜5 | % | ||
| ASTM D-638 | 50%RH｜25 | % | |||
| 拉伸冲击强度 | 长试样23℃ | ASTM D-1822 | DAM｜504 | KJ/m2 | |
| 长试样23℃ | ASTM D-1822 | 50%RH｜1470 | KJ/m2 | ||
| 电气性能 | 介电常数 | 106Hz(cps) | ASTM D-150 | DAM｜3.6 | |
| 106Hz(cps) | ASTM D-150 | 50%RH｜4.6 | |||
| 耗散因数 | 100Hz(cps) | ASTM D-150 | DAM｜0.01 | ||
| 100Hz(cps) | ASTM D-150 | 50%RH｜0.2 | |||
| 介电常数 | 103Hz(cps) | ASTM D-150 | DAM｜3.9 | ||
| 103Hz(cps) | ASTM D-150 | 50%RH｜7.0 | |||
| 耗散因数 | 106Hz(cps) | ASTM D-150 | DAM｜0.02 | ||
| 106Hz(cps) | ASTM D-150 | 50%RH｜0.1 | |||
| 103Hz(cps) | ASTM D-150 | DAM｜0.02 | |||
| 103Hz(cps) | ASTM D-150 | 50%RH｜0.2 | |||
| 体积电阻率 | ASTM D-257 | DAM｜1015 | Ω.cm | ||
| ASTM D-257 | 50%RH｜1013 | Ω.cm | |||
| 介电常数 | 100Hz(cps) | ASTM D-150 | DAM｜4.0 | ||
| 100Hz(cps) | ASTM D-150 | 50%RH｜8.0 | |||
| 热性能 | 荷重形变 | 13.8MPa，50℃ | ASTM D-621 | DAM｜1.4 | % |
| 13.8MPa，50℃ | ASTM D-621 | 50%RH｜- | % | ||
| 热畸变温度 | 18×106Pa | ASTM D-648 | DAM｜90 | ℃ | |
| 18×106Pa | ASTM D-648 | 50%RH｜- | ℃ | ||
| 熔点结晶 | ASTM D-2177 | DAM｜270 | ℃ | ||
| ASTM D-2177 | 50%RH｜- | ℃ | |||
| UL可燃性导级 | UL 94 | DAM｜94 | |||
| UL 94 | 50%RH｜V-2 | ||||
| 脆化温度 | ASTM D-746 | DAM｜-80 | ℃ | ||
| ASTM D-746 | 50%RH｜-65 | ℃ | |||
| 热畸变温度 | (0.5)×106Pa | ASTM D-648 | DAM｜235 | ℃ | |
| (0.5)×106Pa | ASTM D-648 | 50%RH｜- | ℃ | ||
| 导热系数 | DAM｜0.25 | w/mk | |||
| 50%RH｜- | w/mk | ||||
| 线性热膨胀系数 | ASTM D-696 | DAM｜7×10-5 | m/m/℃ | ||
| ASTM D-696 | 50%RH｜- | m/m/℃ | |||
| 熔点 | Fisher Johns法 | ASTM D-789 | DAM｜255 | ℃ | |
| Fisher Johns法 | ASTM D-789 | 50%RH｜255 | ℃ | ||
| 其它性能 | 需氧指数 | ASTM D-2863 | DAM｜28 | % | |
| ASTM D-2863 | 50%RH｜31 | % |