PA66(聚亚己基己二酸酰胺#聚己二酰己二胺#尼龙66) | 70G33L | 塑运塑胶集团 美国杜邦 荷兰D*** 泰国宇部 德国巴斯夫
| 洛氏硬度M | DAM | ASTM D-785 | M101 | ||
| 拉伸强度 | 23℃,DAM | ASTM D-638 | 196.1 | MPa | |
| 埃佐冲击强度 | 23℃,50%RH | ASTM D-256 | 133 | j/m | |
| 23℃,DAM | ASTM D-256 | 107 | j/m | ||
| 断裂伸长率 | 23℃,DAM | ASTM D-638 | 3 | % | |
| 挠曲模量 | 23℃,50%RH | ASTM D-790 | 6205 | MPa | |
| 挤剪强度 | 23℃,DAM | ASTM D-732 | 86 | MPa | |
| 挠曲模量 | 23℃,DAM | ASTM D-790 | 8963 | ||
| 挠曲强度 | 23℃,DAM | ASTM D-790 | 262 | MPa | |
| 拉伸强度 | 23℃,50%RH | ASTM D-638 | 124.1 | MPa | |
| 泰伯磨耗量 | 50%RH | 14 | cycles | ||
| 断裂伸长率 | 23℃,50%RH | ASTM D-638 | 4 | % | |
| 电气性能 | 介电强度 | DAM | ASTM D-149 | 530 | volts/mil |
| (分步法) | ASTM D-149 | 440 | volts/mil | ||
| 体积电阻率 | 100%RH | ASTM D-257 | 10 | ohm-cm | |
| DAM | ASTM D-257 | 10 | ohm-cm | ||
| 介电常数 | DAM@10 | ASTM D-150 | 4.5 | ||
| 100%RH@10 | ASTM D-150 | 10.7 | |||
| 损耗因数 | DAM@10 | ASTM D-150 | 0.02 | ||
| 介电常数 | 100%RH@10 | ASTM D-150 | 25.0 | ||
| 损耗因数 | 100%RH@10 | ASTM D-150 | 0.02 | ||
| 介电常数 | DAM@10 | ASTM D-150 | 3.7 | ||
| 热性能 | 热畸变温度 | 1.8MPa | ASTM D-648 | 249 | ℃ |
| 线性热膨胀系数 | ASTM D-696 | 2.3×10 | m/m/℃ | ||
| 熔点 | DAM | ASTM D-789 | 255 | ℃ | |
| 50%RH | ASTM D-789 | 255 | ℃ |
特性备注:特性：高强度33%玻纤生产厂商：塑运塑胶集团 美国杜邦 荷兰D*** 泰国宇部 德国巴斯夫
用途：热变形温度用于机械部件、电动工具外壳等，可替代杜邦70G33L等。
PA66(聚亚己基己二酸酰胺#聚己二酰己二胺#尼龙66) | 70G33L NC010 | 塑运塑胶集团 美国杜邦 荷兰D*** 泰国宇部 德国巴斯夫
特性备注:玻纤增强生产厂商：塑运塑胶集团 美国杜邦 荷兰D*** 泰国宇部 德国巴斯夫
PA66(聚亚己基己二酸酰胺#聚己二酰己二胺#尼龙66) | 70G33L NC010 (Cond) | 塑运塑胶集团 美国杜邦 荷兰D*** 泰国宇部 德国巴斯夫
特性备注:生产厂商：塑运塑胶集团 美国杜邦 荷兰D*** 泰国宇部 德国巴斯夫
PA66(聚亚己基己二酸酰胺#聚己二酰己二胺#尼龙66) | 70G33L NC010 (Dry) | 塑运塑胶集团 美国杜邦 荷兰D*** 泰国宇部 德国巴斯夫
特性备注:生产厂商：塑运塑胶集团 美国杜邦 荷兰D*** 泰国宇部 德国巴斯夫