SABIC CU6800 PC+ABS 物性表 怎么选料请T&V:153-3800-1126 T:170-8463-1798
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| 线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm
@Thickness 3.20 mm
|
0.0050 - 0.0070 in/in
@Thickness 0.126 in
|
SABIC Method |
| 熔体流动速率 | 23 g/10 min
@Load 2.16 kg, Temperature 260 °C
|
23 g/10 min
@Load 4.76 lb, Temperature 500 °F
|
ASTM D1238 |
| 81 g/10 min
@Load 5.00 kg, Temperature 260 °C
|
81 g/10 min
@Load 11.0 lb, Temperature 500 °F
|
ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 46.0 MPa | 6670 psi | Type I, 50 mm/min; ASTM D638 |
| 抗张强度(屈服) | 59.0 MPa | 8560 psi | Type I, 50 mm/min; ASTM D638 |
| 伸长率 (断裂) | 66 % | 66 % | Type I, 50 mm/min; ASTM D638 |
| 屈服伸长率 | 3.3 % | 3.3 % | Type I, 50 mm/min; ASTM D638 |
| 拉伸模量 | 2.99 GPa | 434 ksi | 50 mm/min; ASTM D638 |
| 弯曲强度 | 88.0 MPa | 12800 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 弯曲模量 | 2.52 GPa | 365 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 悬壁梁缺口冲击强度 | 5.17 J/cm | 9.69 ft-lb/in | ASTM D256 |
| 落锤总能量 | 47.0 J
@Temperature 23.0 °C
|
34.7 ft-lb
@Temperature 73.4 °F
|
ASTM D3763 |
| 热性能 怎么选料请T&V:153-3800-1126 T:170-8463-1798 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 75.6 µm/m-°C
@Temperature -40.0 - 40.0 °C
|
42.0 µin/in-°F
@Temperature -40.0 - 104 °F
|
ASTM E 831 |
| 线性热膨胀系数,横向流动 | 75.6 µm/m-°C
@Temperature -40.0 - 40.0 °C
|
42.0 µin/in-°F
@Temperature -40.0 - 104 °F
|
ASTM E 831 |
| 载荷下热变形温度(0.46 MPa) | 88.0 °C
@Thickness 3.20 mm
|
190 °F
@Thickness 0.126 in
|
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C
@Thickness 3.20 mm
|
165 °F
@Thickness 0.126 in
|
unannealed; ASTM D648 |
| 79.0 °C
@Thickness 6.40 mm
|
174 °F
@Thickness 0.252 in
|
unannealed; ASTM D648 | |
| 维卡软化温度 | 98.0 °C | 208 °F | Rate B/50; ASTM D1525 |
| UL RTI | 60.0 °C | 140 °F | UL 746B |
| UL RTI，机械冲击 | 60.0 °C | 140 °F | UL 746B |
| UL RTI，机械无冲击 | 60.0 °C | 140 °F | UL 746B |
| 可燃性(UL94) | V-1
@Thickness 2.00 mm
|
V-1
@Thickness 0.0787 in
|
UL 94 |
| 5VB
@Thickness 2.00 mm
|
5VB
@Thickness 0.0787 in
|