HDPE/TR-144茂名石化HIPLEX® TR 144, copolymer of ethylene and hexene is tailored for blown film production. Extraordinary melt toughness made possible to get film down to 0.006 mm thickness. Extruded film has high impact resistance, good tear strength, excellent antiblock and good barrier properties, low gel content and excellent sealing and printing properties.
Application:
HIPLEX® TR-144 is suitable for production of composite films, carrier bags and other kinds of packaging. It is also recommended for blow moulding of ***all and medium size containers.
HIPLEX® TR-144 has Health Certificate issued by Institute for Health Protection of Serbia. Also, HIPLEX® TR-144 has Statement of Conformity, which declares product's conformity with the European norms for materials intended to come into contact with foodstuffs. Statement of Conformity is issued by Institute for Public Health, Maribor, Slovenia.
HIPLEX® TR 144 物性表基本信息 添加剂 抗结块剂特性 低速凝固晶点共聚物***的可印刷性己烯共聚单体抗结块性抗撞击性，高良好的热封性良好的熔体强度良好的撕裂强度食品接触的合规性阻隔树脂用途 Blown Containers包装薄膜吹塑成型应用袋子机构评级 EC 1907/2006 (REACH) 形式 粒子加工方法 吹塑薄膜吹塑成型
物理性能 额定值 单位制 测试方法密度 0.947 g/cm³ ISO 1183 熔流率（熔体流动速率） (190°C/2.16 kg) 0.18 g/10 min ISO 1133 抗环境应力开裂 (条件 B, F50) > 1000 hr ISO 22088 硬度 额定值 单位制 测试方法肖氏硬度 (邵氏 D) 64 ISO 868 机械性能 额定值 单位制 测试方法拉伸应力 ISO 527-2 屈服 21.0 MPa ISO 527-2 断裂 32.0 MPa ISO 527-2 拉伸应变 (断裂) 900 % ISO 527-2 薄膜 额定值 单位制 测试方法薄膜厚度 - 经测试 25 µm 拉伸应力 ISO 527-3 MD : 屈服, 25 µm 24.0 MPa ISO 527-3 TD : 屈服, 25 µm 19.0 MPa ISO 527-3 MD : 断裂, 25 µm 40.0 MPa ISO 527-3 TD : 断裂, 25 µm 32.0 MPa ISO 527-3 伸长率 ISO 527-3 MD : 断裂, 25 µm 550 % ISO 527-3 TD : 断裂, 25 µm 690 % ISO 527-3 落锤冲击 (25 µm) 80 g ASTM D1709 Elmendorf Tear Strength 1 ASTM D1922 MD : 25.0 µm 27.0 kN/m ASTM D1922 TD : 25.0 µm 270.3 kN/m ASTM D1922 补充信息 额定值 单位制 吹气模制温度 2 195 到 220 °C 冲击性能 额定值 单位制 测试方法悬壁梁缺口冲击强度 无断裂 ISO 180 热性能 额定值 单位制 测试方法维卡软化温度 124 °C ISO 306