HDPE/M80064沙特SABIC--SABIC® HDPE M80064 is a high density polyethylene injection moulding grade with a narrow molecular weight distribution. It is typically used for injection moulding applicati*** where rigidity, toughness and warp resistance are required. SABIC® HDPE M80064 is available with UV stabilizer as SABIC® HDPE M80064S.
Typical applicati***.
SABIC® HDPE M80064 is typically used for the manufacture of injection moulded cases, crates, trays, industrial pails and other similar items.
This product is not intended for and must not be used in any pharmaceutical/medical applicati***
特性 高密度抗弯曲韧性良好窄分子量分布中等硬度用途 工业应用桶装货箱加工方法 ***成型
物理性能 额定值 单位制 测试方法密度 0.964 g/cm³ ISO 1183 熔流率（熔体流动速率） ISO 1133 190°C/2.16 kg 8.0 g/10 min ISO 1133 190°C/5.0 kg 22 g/10 min ISO 1133 抗环境应力开裂 1(60°C, 3.00 mm, Rhodacal-DS10, 模压成型) 40.0 hr 内部方法硬度 额定值 单位制 测试方法肖氏硬度 (邵氏 D, 模压成型) 65 ISO 868 机械性能 额定值 单位制 测试方法拉伸模量 (2.00 mm, 模压成型) 1450 MPa ISO 527-2/1BA/50 拉伸应力 ISO 527-2/1BA/50 屈服, 2.00 mm, 模压成型 32.0 MPa ISO 527-2/1BA/50 断裂, 2.00 mm, 模压成型 15.0 MPa ISO 527-2/1BA/50 拉伸应变 (断裂, 2.00 mm, 模压成型) > 200 % ISO 527-2/1BA/50 弯曲模量 (2.00 mm, 模压成型) 1700 MPa ISO 178 弯曲应力 (2.00 mm, 模压成型) 32.0 MPa ISO 178 冲击性能 额定值 单位制 测试方法悬壁梁缺口冲击强度 (23°C, 模压成型) 4.0 kJ/m² ISO 180/A 热性能 额定值 单位制 测试方法热变形温度 (0.45 MPa, 未退火) 95.0 °C ISO 75-2/B 维卡软化温度 129 °C ISO 306/A 溶融温度（DSC） 135 °C ISO 11357-3 Enthalpy Change 229 J/g ISO 11357-3 *** 额定值 单位制 加工（熔体）温度 230 到 275 °C 模具温度 32.0 到 38.0 °C 注塑压力 69.0 到 89.0 MPa