Lustran® ABS 348
***丁二烯***
Styrolution
产品说明：
Lustran® ABS 348 resin is an injection molding grade of ABS (Acrylonitrile butadiene styrene). It is a medium impact, high-gloss ABS, ***ailable in natural (000000), snowhite (012002), and selected colors.
Lustran ABS 348 resin combines a good balance of physical properties, intermediate abuse resistance, and rigidity. Typical applicati*** include components of intr***enous (IV) systems, diagnostic test kits, and surgical instruments. As with any product, use of Lustran ABS 348 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
Lustran ABS 348 resin combines a good balance of physical properties, intermediate abuse resistance, and rigidity. Typical applicati*** include components of intr***enous (IV) systems, diagnostic test kits, and surgical instruments. As with any product, use of Lustran ABS 348 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
Lustran® ABS 348 物性表
| 基本信息 | |
|---|---|
| 黄卡编号 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 多点数据 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | 1.06 | g/cm³ | ASTM D792 |
| 特定体积 | 0.940 | cm³/g | ASTM D792 |
| 熔流率（熔体流动速率） | ASTM D1238 | ||
| 220°C/10.0 kg | 14 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 5.0 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 | 0.40 到 0.60 | % | ASTM D955 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 洛氏硬度 (R 级) | 112 | ASTM D785 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 | 2620 | MPa | ASTM D638 |
| 抗张强度 (屈服) | 48.3 | MPa | ASTM D638 |
| 弯曲模量 | 2690 | MPa | ASTM D790 |
| 弯曲强度 (屈服) | 75.8 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 悬壁梁缺口冲击强度 | ASTM D256 | ||
| -40°C, 3.18 mm | 48 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 210 | J/m | ASTM D256 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度 | ASTM D648 | ||
| 0.45 MPa, 未退火, 12.7 mm | 92.8 | °C | ASTM D648 |
| 0.45 MPa, 退火, 12.7 mm | 100 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 12.7 mm | 85.6 | °C | ASTM D648 |
| 1.8 MPa, 退火, 12.7 mm | 95.6 | °C | ASTM D648 |
| 维卡软化温度 | 107 | °C | ASTM D1525 1 |
| 线形热膨胀系数 - 流动 | 8.1E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (1.50 mm) | 80.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 80.0 | °C | UL 746 |
| RTI (1.50 mm) | 80.0 | °C | UL 746 |
| 可燃性 | 额定值 | 测试方法 | |
|---|---|---|---|
| UL 阻燃等级 | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| *** | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | |||
| A | 82.2 到 87.8 | °C | |
| B | 71.1 到 76.7 | °C | |
| 干燥时间 | |||
| A | 2.0 | hr | |
| B | 4.0 | hr | |
| 建议的***大水分含量 | < 0.10 | % | |
| 建议***量 | 50 到 75 | % | |
| 料筒后部温度 | 235 到 249 | °C | |
| 料筒中部温度 | 241 到 254 | °C | |
| 料筒前部温度 | 246 到 260 | °C | |
| 射嘴温度 | 246 到 260 | °C | |
| 加工（熔体）温度 | 246 到 274 | °C | |
| 模具温度 | 43.3 到 65.6 | °C | |
| 注塑压力 | 68.9 到 110 | MPa | |
| ***速度 | 快速 | ||
| 背压 | 0.00 到 0.172 | MPa | |
| 锁模力 | 2.8 到 5.5 | kN/cm² | |
| 垫层 | < 6.35 | mm | |
| 螺杆长径比 | 20.0:1.0 | ||
| 螺杆压缩比 | 2.5:1.0 |
| ***说明 |
|---|
| No regrind allowed for medical applicati***Hold Pressure: 50 to 75% of Injection PressureScrew Speed: Moderate |
食品级ABS PA-737台湾奇美PA-737
食品级ABS HP20沙伯基础HP20
***食品级ABS HP30沙伯基础HP30
食品级ABS MG38F沙伯基础HP20
***级ABS HMG47MD沙伯基础HP20
***级ABS 2802HD巴斯夫
***级ABS 2802-TR巴斯夫
高透明ABS PA- 758台湾奇美 PA- 758
高透明ABS 920 日本东丽920
高透明ABS SX-200日本旭化成 SX-200
高透明ABS TR-577 韩国LG TR-577
高透明ABS TR-558AI 韩国LG TR-558AI
高透明ABS TH-21 日本电气化 TH-21
防火抗紫外线ABS FR15U美国GE FR15U
防火ABS FR15美国GE FR15