低粘度PC/1300-30韩国LG产品说明： LUPOY PC 1300-30 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.
Main Characteristics:
Applicati***:
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
1.20 |
g/cm³ |
ASTM D792 |
| 熔流率（熔体流动速率） (300°C/1.2 kg) |
30 |
g/10 min |
ASTM D1238 |
| 收缩率 - 流动 |
0.50 到 0.70 |
% |
ASTM D955 |
| 吸水率 |
|
|
ASTM D570 |
| 23°C, 24 hr |
0.15 |
% |
ASTM D570 |
| 平衡, 23°C, 50% RH |
0.32 |
% |
ASTM D570 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 拉伸模量 |
2340 |
MPa |
ASTM D638 |
| 抗张强度 |
|
|
ASTM D638 |
| 屈服, 23°C 1 |
60.0 |
MPa |
ASTM D638 |
| 极限 |
61.0 |
MPa |
ASTM D638 |
| 伸长率 |
|
|
ASTM D638 |
| 屈服 |
6.0 |
% |
ASTM D638 |
| 断裂 |
150 |
% |
ASTM D638 |
| 弯曲模量 |
2410 |
MPa |
ASTM D790 |
| 弯曲强度 |
96.0 |
MPa |
ASTM D790 |
| 冲击性能 |
额定值 |
单位制 |
测试方法 |
| 悬壁梁缺口冲击强度 2(23°C, 3.20 mm) |
700 |
J/m |
ASTM D256 |
| 无缺口悬臂梁冲击 (23°C) |
无断裂 |
|
ASTM D256 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
ASTM D648 |
| 0.45 MPa, 退火, 4.00 mm |
139 |
°C |
ASTM D648 |
| 1.8 MPa, 未退火, 4.00 mm |
122 |
°C |
ASTM D648 |
| 1.8 MPa, 退火, 4.00 mm |
136 |
°C |
ASTM D648 |
| 维卡软化温度 |
144 |
°C |
ASTM D1525 3 |
| 球压温度 |
> 125 |
°C |
IEC 60598-1 |
| 线形热膨胀系数 - 流动 (-40 到 82°C) |
6.8E-5 |
cm/cm/°C |
ASTM D696 |
| 电气性能 |
额定值 |
单位制 |
测试方法 |
| 体积电阻率 (23°C) |
2.0E+17 |
ohms·cm |
ASTM D257 |
| 介电强度 |
17 |
kV/mm |
ASTM D149 |
| 介电常数 (60 Hz) |
3.00 |
|
ASTM D150 |
| 耗散因数 (60 Hz) |
1.0E-3 |
|
ASTM D150 |
| 漏电起痕指数 (2.00 mm) |
250 |
V |
IEC 60112 |
| 可燃性 |
额定值 |
单位制 |
测试方法 |
| UL 阻燃等级 |
|
|
UL 94 |
| 0.500 mm |
V-2 |
|
UL 94 |
| 1.60 mm |
V-2 |
|
UL 94 |
| 2.50 mm |
V-2 |
|
UL 94 |
| 3.00 mm |
V-2 |
|
UL 94 |
| 热灯丝点火温度 4(2.00 mm) |
850 |
°C |
IEC 60695-2-13 |
| 极限氧指数 |
26 |
% |
ASTM D2863 |
| 平均燃烧程度 |
3 |
cm |
ASTM D635 |
| 光学性能 |
额定值 |
单位制 |
测试方法 |
| 折射率 |
1.586 |
|
ASTM D542 |
| 透射率 |
89.0 |
% |
ASTM D1003 |
| 雾度 |
0.70 到 1.5 |
% |
ASTM D1003 |