POM GB-25日本宝理---Note: glass beads 25% reinforced, low warpage
Gb-25 physical property table
Test method of physical performance rating unit
Density 1.59 ISO 1183
Mechanical properties - rating units - Test methods
Tensile strength - 59 MPa - ISO 527-1, - 2
Fracture strain - 10% ISO 527-1, - 2
Tensile modulus of elasticity - 4000 MPa - ISO 527-1, - 2
Bending strength 104 MPa ISO 178
Bending modulus 3800 MPa ISO 178
Notched impact strength of simply supported beam: 3.6 kJ / M ISO 179 / 1ea
Electrical performance rating unit test method
Dielectric failure strength 18 kV / mm IEC 60243-1
Volume resistivity: 8 × 10 Ω. Cm IEC 60093
Surface resistivity > 5 × 10 Ω IEC60093
Thermal performance rating unit test method
Hot deformation temperature - 123 ℃ ISO 75-1, - 2
Coefficient of linear expansion ISO 11359-2
(flow direction) 9
(vertical) 9
Flame retardant HB
POM于50年代末期由杜邦公司研制开发，是目前世界三大通用工程塑料之一。POM具有金属的硬度、强度和钢性，优良的耐疲劳性，具于弹性， POM还有较好的耐***性。POM自生产开始广泛用于电子电气、机械、仪表、日用轻工、汽车、建材、农业等领域。由于POM的成本低于其他工程塑料，然而替代了被金属占领的市场，在新的应用领域中也表现出很好的增长趋势，如***技术、运动器械等方面。
POM分子结构规整，结晶度高，表面硬度大，在摩擦滑动过程中其大分子易沿摩擦方向取向而强化，键能大，分子内聚能高，因而POM具有良好的耐磨自润滑性能。但仍难以满足高负荷、高速、高温等工作条件的要求，需进一步改善POM的耐磨性能。提高POM耐磨性能有两种方法：一种是化学改性。利用接技、嵌段等手段在POM分子链上引入具有润滑性的链段。另一种是物理共混改性。日本塑料公司开发的Duracon NW-02是一种由润滑性聚合物与POM接枝而成的润滑改性剂。在相同载荷与滑动速度下，Duracon NW-02的滑动表面温度比未经改性的一般共聚POM低30%~50%。