乐天PC PC-1100---Product Description:Medium viscosity, high impact strength. High tensile strength, flexural strength, and elastic modulus
Hopelex pc-1100 physical property table
essential information
characteristic
Rigid, high tensile strength, impact resistance, high and medium viscosity
RoHS compliance
RoHS compliance
Processing method
injection molding
Physical performance rating unit system test method
Specific gravity: 1.20 g / cm 3 ASTM D792
Melt flow rate (melt flow rate) (300 ° C / 1.2 kg) 10 g / 10 min ASTM d1238
Shrinkage - flow 0.50 to 0.70% ASTM D955
Mechanical properties rating unit system test method
Tensile strength 1 (yield) 61.8 MPa ASTM D638
Elongation 2 (break) > 100% ASTM D638
Bending modulus 3 2350 MPa ASTM D790
Bending strength 4 (yield) 90.2 MPa ASTM D790
Impact performance rating unit system test method
Notched impact strength of cantilever beam (23 ° C, 3.18 mm) 780 J / M ASTM D256
Thermal performance rating unit test method
Hot deformation temperature under load ASTM D648
45 MPa, UN annealed at 143 ° C ASTM D648
1.8 MPa, UN annealed at 132 ° C ASTM D648
Vicat softening temperature 150 ° C ASTM d1525 5
Optical performance rating unit system test method
Refractive index: 1.585 ASTM d542
Transmittance: 89.0% ASTM d1003
Haze < 0.80% ASTM d1003
Injection rating unit system
Drying temperature: 120 ° C
Drying time: 4.0 HR
Recommended maximum moisture content 0.020%
Recommended maximum recycling ratio of 20%
Hopper temperature from 60.0 to 80.0 ° C
Barrel rear temperature 290 to 310 ° C
The temperature in the middle of the barrel is 280 to 300 ° C
Temperature at front of barrel 270 to 290 ° C
Nozzle temperature 280 to 300 ° C
Processing (melt) temperature 290 to 310 ° C
Mold temperature: 60.0 to 90.0 ° C