PC HF-3200H--Infino hf-3200h is a polycarbonate (PC) product with glass fiber reinforced filler. It is ***ailable in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Main characteristics: flame retardant / rated flame.
PC Hf-3200h physical property table
essential information
Yellow card number
E115797-100468271
Filler / reinforcement
Glass fiber reinforced material
Physical performance rating unit system test method
Specific gr***ity: 1.37 g / cm? ASTM D792, ISO 1183
Melt flow rate (melt flow rate) (250 ° C / 10.0 kg) 11 g / 10 min ASTM d1238, ISO 1133
Ash content 19% ISO 3451
Impact performance rating unit system test method
Notched impact strength of simply supported beam 9 (23 ° C) 14 kJ / M? ISO 179 / 1ea
Notched impact strength of cantilever beam
23°C, 3.18 mm 140 J/m ASTM D256
23°C 10 12 kJ/m² ISO 180/1A
Thermal performance rating unit test method
Thermal deformation temperature under load
0.45 MPa, UN annealed, 6.40 mm at 145 ° C, ASTM D648
0.45 MPa, UN annealed, 4.00 mm at 146 ° C ISO 75-2 / b
45 MPa, annealed at 146 ° C ISO 75-2 / b
1.8 MPa, UN annealed, 6.40 mm at 140 ° C, ASTM D648
1.8 MPa, UN annealed, 4.00 mm 142 ° C ISO 75-2 / A
1.8 MPa, annealed, 4.00 mm 142 ° C ISO 75-2 / A
Vicat softening temperature 150 ° C ISO 306 / ***
Flammability rating test method
UL flame retardant grade (1.50 mm) V-2 UL 94
Injection rating unit system
drying temperature
-- 120 °C
Hot air dryer 110 ° C
drying time
--4.0 to 6.0 HR
Hot air dryer 2.0 to 4.0 HR
Recommended maximum moisture content < 0.050%
The temperature at the back of the barrel is 250 to 260 ° C
The temperature in the middle of the barrel is 260 to 270 ° C
The temperature at the front of the barrel is 280 to 285 ° C
Nozzle temperature 285 ° C
Mold temperature: 70.0 to 100 ° C
Injection pressure: 68.6 to 226 MPa
Back pressure: 0.490 to 1.96 MPa
Screw speed: 50 to 150 rpm