PC LB-1010W--Infino lb-1010w is a polycarbonate (PC) product,. It is ***ailable in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The main characteristics are: flame retardant / rated flame
Infino lb-1010w physical property table
essential information
Yellow card number
E115797-219702
Physical performance rating unit system test method
Specific gr***ity: 1.26 g / cm? ASTM D792, ISO 1183
Melt flow rate (melt flow rate) (250 ° C / 10.0 kg) 48 g / 10 min ASTM d1238, ISO 1133
Shrinkage - flow (3.20 mm) 0.50 to 0.70% ASTM D955
Impact performance rating unit system test method
Notched impact strength of simply supported beam 9 (23 ° C) 47 kJ / M? ISO 179 / 1ea
Notched impact strength of cantilever beam
23°C, 3.18 mm 490 J/m ASTM D256
23°C, 6.35 mm 370 J/m ASTM D256
23°C 10 43 kJ/m² ISO 180/1A
Thermal performance rating unit test method
Hot deformation temperature
0.45 MPa, UN annealed, 4.00 mm at 132 ° C ISO 75-2 / b
45 MPa, annealed at 133 ° C ISO 75-2 / b
1.8 MPa, UN annealed, 6.40 mm, 129 ° C, ASTM D648
1.8 MPa, UN annealed, 4.00 mm 117 ° C ISO 75-2 / A
1.8 MPa, annealed, 4.00 mm 123 ° C ISO 75-2 / A
Vicat softening temperature
-- 139 °C ISO 306/***
-- 141 °C ISO 306/B120
Flammability rating test method
UL flame retardant grade (0.750 mm) V-2 UL 94
Injection rating unit system
drying temperature
-- 120 °C
Hot air dryer 110 ° C
drying time
--2.0 to 6.0 HR
Hot air dryer 2.0 to 4.0 HR
Recommended maximum moisture content < 0.050%
Barrel rear temperature 240 to 250 ° C
The temperature in the middle of the barrel is 260 to 270 ° C
Barrel front temperature 280 to 290 ° C
Nozzle temperature 290 to 310 ° C
Mold temperature from 40.0 to 100 ° C
Injection pressure: 49.0 to 245 MPa
Back pressure: 0.490 to 1.96 MPa
Screw speed: 50 to 150 rpm