PA nylon: the mechanical properties of PA, such as tensile and compressive strength changes with temperature and moisture absorption, so water is the plasticizer of PA. after adding glass fiber, its tensile and compressive strength can be increased by about 2 times, and the temperature resistance ability is also improved correspondingly. PA itself has high wear resistance, so it can be operated without lubrication. If you want to get special lubrication effect, you can add sulfide into PA.
PA6 CM1016G-45---CM1016G-45
PA6 | 聚已内酰胺#尼龙6
日本东丽
CM1016G-45 物性表
物理性能 额定值 单位 测试方法
填充含量 45 Wt%
比重 1.50 D792
吸水率 D570
(23℃,24hrs) 0.9 %
(23℃,水中) 5.3 %
洛氏硬度 (23℃) 121 R D785
机械性能 额定值 单位 测试方法
拉伸屈服强度 D638
(-40℃) 290 MPa
(23℃) 205 MPa
(80℃) 120 MPa
断裂伸长率 D638
(-40℃) 4.5 %
(23℃) 5.0 %
(80℃) 8.0 %
弯曲强度 D790
(-40℃) 330 MPa
(23℃) 290 MPa
(80℃) 160 MPa
弯曲模量 D790
(-40℃) 14.0 Gpa
(23℃) 12.0 Gpa
(80℃) 6.2 Gpa
压缩强度 (23℃) 190 MPa D695
肖氏强度 (23℃) 95 MPa D732
冲击强度 D256
(-40℃) 125 J/M
(23℃) 155 J/M
(-40℃) 90 KJ/m
(23℃) 100 KJ/m
热性能 额定值 单位 测试方法
熔点 225 ℃ DSC
线膨胀系数 0.40 W/M.℃
热变形温度 D648
(0.46Mpa) 225 ℃
(1.86MPa) 215 ℃
阻燃性 HB