PA6 CM1017---Cm1017 is a polyamide 6 (nylon 6) product,. It is available in North America, Europe or Asia Pacific. The main characteristics are: flame retardant / rated flame
Unit system test method for physical properties after drying and adjustment
Density (23 ° C) 1.13 -- g / cm 3 ISO 1183
Shrinkage flow direction internal method
1.00 mm 1 0.50 to 1.0 --% internal method
3.00 mm2 1.0 to 1.6 --% internal method
Water absorption ISO 62
23°C, 24 hr 1.8 -- % ISO 62
Saturated, 23 ° C 11 --% ISO 62
Unit system test method for hardness, drying and adjustment
Rockwell hardness ISO 2039-2
R scale, 80 ° C 83 -- ISO 2039-2
R scale, 23 ° C 119 90 ISO 2039-2
Mechanical properties - unit system test method after drying and adjustment
Tensile stress ISO 527-2
-40°C 120 115 MPa ISO 527-2
23°C 85.0 40.0 MPa ISO 527-2
80°C 30.0 20.0 MPa ISO 527-2
Tensile strain ISO 527-2
Yield, 23 ° C 1.5 --% ISO 527-2
Fracture, 23 ° C 38.50% ISO 527-2
Bending modulus ISO 178
-40°C 3900 3600 MPa ISO 178
23°C 3000 1000 MPa ISO 178
80°C 800 400 MPa ISO 178
Bending stress ISO 178
-40°C 145 140 MPa ISO 178
23°C 120 45.0 MPa ISO 178
80°C 50.0 30.0 MPa ISO 178
Compressive stress (23 ° C) 85.0 -- MPa ISO 604
Shear strength (23 ° C) 75.0 ~ 70.0 MPa ASTM d732
Taber abrasion resistance (1000 cycles) 3.00 to 4.00 -- Mg ISO 9352
Friction coefficient - vs. metal 3 0.150 to 0.200 -- Suzuki Method
Impact performance - unit system test method after drying and adjustment
Notched impact strength of simply supported beams ISO 179
-40°C 2.5 12 kJ/m² ISO 179
23°C 4.0 31 kJ/m² ISO 179
Notchless impact strength of simply supported beams ISO 179
-No fracture at 40 ° C - ISO 179
No fracture at 23 ° C -- ISO 179
Unit system test methods for thermal performance, drying and conditioning
Hot deformation temperature (0.45 MPa, UN annealed) 190 - - C ISO 75-2 / b
Melting temperature: 225 - - C DSC
Linear coefficient of thermal expansion - flow 8.0e-5 -- cm / cm / ° C ISO 11359-2
Specific heat 1900 -- J / kg / ℃
Thermal conductivity: 0.25 -- w / M / K