PA6 1015GC6---1015gc6 is a polyamide 6 (nylon 6) product containing 30% glass fiber reinforcement. It can be processed by injection molding and is available in North America.
Features include:
Flame retardant / rated flame
Chemical resistance
high strength
hard
Impact resistance
The chemical and physical properties of polyamide-6 are similar to nylon 66, however, it has a low melting point and a wide range of process temperature. Its impact resistance and solubility are better than nylon 66 plastics, but its moisture absorption is stronger.
物理性能 干燥 调节后的 单位制 测试方法
比重 1.36 -- g/cm³ ASTM D792
收缩率 - 流动 0.20 到 0.70 -- % ASTM D955
吸水率 (饱和) 6.6 -- % ASTM D570
硬度 干燥 调节后的 单位制 测试方法
洛氏硬度 ASTM D785
M 级 100 -- ASTM D785
R 级 120 110 ASTM D785
机械性能 干燥 调节后的 单位制 测试方法
抗张强度 (屈服) 167 98.0 MPa ASTM D638
伸长率 (屈服) 5.0 6.0 % ASTM D638
弯曲模量 7840 4410 MPa ASTM D790
弯曲强度 (屈服) 245 127 MPa ASTM D790
压缩强度 27.4 15.7 MPa ASTM D695
剪切强度 85.2 58.8 MPa ASTM D732
冲击性能 干燥 调节后的 单位制 测试方法
悬壁梁缺口冲击强度 ASTM D256
-30°C 78 140 J/m ASTM D256
23°C 110 230 J/m ASTM D256
热性能 干燥 调节后的 单位制 测试方法
载荷下热变形温度 (1.8 MPa, 未退火) 215 -- °C ASTM D648
熔融温度 215 到 225 -- °C
线形热膨胀系数 - 流动 2.5E-5 -- cm/cm/°C ASTM D696
RTI Elec (0.794 mm) 65.0 -- °C UL 746
RTI Imp (0.794 mm) 65.0 -- °C UL 746
RTI (0.794 mm) 65.0 -- °C UL 746
电气性能 干燥 调节后的 单位制 测试方法
体积电阻率 1.0E+15 1.0E+12 ohms·cm ASTM D257
介电常数 ASTM D150
60 Hz 4.20 -- ASTM D150
1 MHz 3.80 -- ASTM D150
耗散因数 ASTM D150
60 Hz 0.010 -- ASTM D150
1 MHz 0.020 -- ASTM D150
耐电弧性 (0.794 mm) 121 -- sec ASTM D495
可燃性 干燥 调节后的 单位制 测试方法
UL 阻燃等级 (0.794 mm) HB -- UL 94
*** 干燥 单位制
建议的***大水分含量 0.10 %
料筒后部温度 240 °C
料筒中部温度 265 °C
料筒前部温度 275 °C
射嘴温度 275 °C
加工(熔体)温度 285 °C
模具温度 70.0 到 80.0 °C
注塑压力 83.2 MPa
背压 9.80 MPa
螺杆转速 100 到 130 rpm