PA6 BG30X产品说明：PA 6, 30 % glass fibers/glass spheres, injection molding, low tendency to warp
PA 6，30%玻璃纤维/玻璃球，注塑成型，低翘曲倾向
Thermal properties - unit system test method after drying
Thermal deformation temperature under load
0.45 MPa, annealed, 39.9 MM 200 -- ° C ASTM D648
0.45 MPa, annealed 210 -- ° C ISO 75-2/b
1.8 MPa, annealed 190 -- ° C ISO 75-2/a
1.8 MPa, annealed, 3.99 mm 180 -- ° C ASTM D648
Vicat softening temperature > 200 -- ° C ISO 306/***, ISO 306/b120
Melting temperature 10 222 -- ° C ISO 11357-3
Linear coefficient of thermal expansion ISO 11359-2
Flow: 23 to 55 ° C 3.0e-5 -- cm/cm/ ° C ISO 11359-2
Transverse: 23 to 55 ° C 9.0e-5 -- cm/cm/ ° C ISO 11359-2
RTI Elec (1.50 mm) 120 -- °C UL 746
RTI Imp (1.50 mm) 90.0 -- °C UL 746
RTI (1.50 mm) 125 -- °C UL 746
Electrical performance - unit system test method after drying and adjusting
Surface resistivity: 1.0e+14 to 1.0e+16 1.0e+12 to 1.0e+13 ohms IEC 60093
Volume resistivity (23 ° C) 1.0e + 15 1.0e + 11 to 1.0e + 12 ohms · cm IEC 60093
Dielectric strength IEC 60243-1
23°C, 1.00 mm 36 30 kV/mm IEC 60243-1
23°C, 3.00 mm 35 35 kV/mm IEC 60243-1
Dielectric constant IEC 60250
23°C, 50 Hz 11 4.50 10.0 IEC 60250
23°C, 1 MHz 12 4.00 5.00 IEC 60250
23°C, 100 Hz 4.50 16.0 IEC 60250
23°C, 1 MHz 4.00 4.80 IEC 60250
Dissipation factor IEC 60250
23°C, 50 Hz 0.015 0.20 IEC 60250
23°C, 100 Hz 0.013 0.31 IEC 60250
23°C, 1 MHz 0.018 0.020 0.10 0.060 IEC 60250
Arc resistance 13-110 sec ASTM D495
Leakage mark index
Solution a 400 - V IEC 60112
-- -- 450 V ASTM D3638
Test method of unit system after flammability drying
UL flame retardant rating UL 94
1.50 mm HB -- UL 94
1.60 mm HB -- UL 94
3.00 mm HB -- UL 94
3.20 mm HB -- UL 94
Flammability index of hot wire (2.00 mm) 650 -- ° C IEC 60695-2-12
Limit oxygen index 14 23 --% ISO 4589-2
Injection drying unit system test method
Drying temperature - dry air dryer 80.0 ° C
Drying time - dry air dryer 2.0 to 6.0 HR
Processing (melt) temperature 270 to 290 ° C
Mold temperature 80.0 to 120 ° C