PA6 BKV30H2.0 BK---PA 6, 30 % glass fibers, injection molding, heat-aging stabilized
Unit system test method for physical properties after drying and adjustment
proportion
-- 1.36 -- g/cm³ ASTM D792
23°C 1.38 -- g/cm³ ISO 1183
Apparent density: 0.70 -- g / cm 3 ISO 60
Water absorption ISO 62
Saturated, 23 ° C 7.0 --% ISO 62
Balanced, 23 ° C, 50% RH 2.1 --% ISO 62
Mechanical properties - unit system test method after drying and adjustment
Tensile modulus
23°C 1 9200 5600 MPa ASTM D638
23°C 9600 5900 MPa ISO 527-2/1
Tensile strength
Fracture, 23 ° C 180 100 MPa ASTM D638
Fracture, 23 ° C 170 100 MPa ISO 527-2 / 5
elongation
Fracture, 23 ° C 3.0 6.0% ASTM D638
Fracture, 23 ° C 3.5 6.5% ISO 527-2 / 5
Tensile creep modulus (1000 HR) - 4100 MPa ISO 899-1
Bending modulus
23°C 8300 5000 MPa ASTM D790
23°C 2 8500 5100 MPa ISO 178/A
bending strength
23°C 280 170 MPa ASTM D790
3.5% strain, 23 ° C 265 140 MPa ISO 178 / A
23°C 3 280 170 MPa ISO 178/A
Flexural Strain at Flexural Strength 4(23°C) 4.0 6.0 % ISO 178/A