PA6 F223-D荷兰D***---F223-d is a polyamide 6 (nylon 6) material,. The product is available in North America, Europe or Asia Pacific region, and the processing method is injection molding.
The main characteristics of akulon? F223-d are as follows:
Flame retardant / rated flame
Medium viscosity
Unit system test method for physical properties after drying and adjustment
Density: 1.13 -- g / cm 3 ISO 1183
Shrinkage: ISO 294-4
Vertical flow direction 1.1 --% ISO 294-4
Flow direction 1.1 --% ISO 294-4
Water absorption ISO 62
Saturated, 23 ° C 10 --% ISO 62
Balanced, 23 ° C, 50% RH 2.8 --% ISO 62
Viscosity 129 -- cm 3 / g ISO 307
Mechanical properties - unit system test method after drying and adjustment
Tensile modulus 3200 1000 MPa ISO 527-2
Tensile stress (yield) 85.0 45.0 MPa ISO 527-2
Tensile strain (yield) 4.0 25% ISO 527-2
Nominal tensile breaking strain 20 > 50% ISO 527-2
Bending modulus 2600 -- MPa ISO 178
Bending stress: 100 -- MPa ISO 178
Unit system test method for flammability, drying and adjustment
Flammability class - IEC 60695-11-10, - 20
0.750 mm V-2 -- IEC 60695-11-10, -20
1.50 mm V-2 -- IEC 60695-11-10, -20
Flammability index (1.50 mm) 800 - - C IEC 60695-2-12
Hot filament ignition temperature (1.50 mm) 775 - - C IEC 60695-2-13
Limiting oxygen index 26 --% ISO 4589-2
Injection drying unit system
Drying temperature: 80.0 ° C
Drying time is from 4.0 to 8.0 hr
Barrel rear temperature 230 to 235 ° C
The temperature in the middle of the barrel is 235 to 250 ° C
Barrel front temperature 240 to 260 ° C
Nozzle temperature 240 to 270 ° C
Processing (melt) temperature 240 to 275 ° C
Mold temperature: 50.0 to 80.0 ° C
The injection speed was medium to high
Back pressure 3.00 to 10.0