品级：高耐冲级
规格：HP8250
特性：高耐冲性,一般成型用
用途：家电外壳、电视机外壳、终端机外壳、电脑主机面板
台化HIPS-HP8250 聚***塑胶粒物性
TAIRIREX Polystyrene resin c***olidated property data sheet
| 項 目 | *** 位 | 試驗方法 | 試驗條件 | HP8250 |
| Property | Unit | Test Method | Test Condition | |
| 抗張強度 | kg/cm2 | ASTM | 23℃ | 220 |
| Tensile Strength | (MPa) | D-638 | -22 | |
| - | - | (ISO527) | - | |
| 伸長率 | % | ASTM | 23℃ | 40 |
| Tensile Elongation | D-638 | |||
| - | (ISO527) | |||
| ***曲強度 | kg/cm2 | ASTM | 23℃ | 440 |
| Flexural Strength | (MPa) | D-790 | -43 | |
| - | - | (ISO178) | - | |
| ***曲模數 | kg/cm2*104 | ASTM | 23℃ | 2.3 |
| Flexural Modulus | (MPa) | D-790 | -2260 | |
| - | - | (ISO178) | - | |
| Izod衝擊強度 | kg-cm/cm | ASTM | 23℃ | 11 |
| Izod | (J/m) | D-256 | 1/4''厚 | -108 |
| Impact Strength | - | (ISO R180) | - | - |
| ***氏軟化點 | ℃ | ASTM | Annealed | 95 |
| Vicat Softening | D-1525 | 80℃×2Hr | ||
| Temperature | (ISO306B) | 1/8''厚 | ||
| ******形溫度 | ℃ | ASTM | Annealed | 88 |
| Heat Deflection | D-648 | 80℃×2Hr | ||
| Temperature | (ISO 75/A) | 1/8''厚 | ||
| 熔融指數 | g/10 min | ASTM | 200℃×5Kg | 5.5 |
| Melt | D-1238 | (49N) | ||
| Flow Index | (ISO1133) | - | ||
| 殘留***體 | ppm max. | - | - | 700 |
| Residual Monomer | ||||
| 收縮率 | % | FCFC | 23℃ | 0.4~0.6 |
| Molding | Method | |||
| Shrinkage | - | |||
| 比 重 | - | ASTM | 23℃/23℃ | 1.04 |
| Specific Gr***ity | D-792 | |||
| - | (ISO1183) | |||
| 燃燒性 | - | UL-94 | FILE NO. | 1/16"HB |
| Flammability | E162823 | NC |