铝合金焊接材料
|
|
ESAB |
技术标准 |
熔敷金属力学性能 |
熔敷金属化学成分（％） |
||||||||
|
SFA/AWS A5.10 |
DIN 1732 |
屈服值Mpa |
抗拉强度Mpa |
延伸率％ |
冲击值 |
Si |
Mn |
Zn |
Fe |
Al |
||
|
气保焊丝 |
OK Autrod 1100 |
ER1100 |
SG Al99.5 |
35 |
75 |
33 |
|
＜0.2 |
0.01 |
0.01 |
0.2 |
＞99.5 |
|
OK Autrod 4043 |
ER4043 |
SG AlSi5 |
55 |
165 |
18 |
|
5.0 |
0.01 |
0.02 |
0.2 |
bal. |
|
|
OK Autrod 4047 |
ER4047 |
SG AlSi12 |
80 |
170 |
12 |
|
12.0 |
0.01 |
0.02 |
＜0.2 |
bal. |
|
|
OK Autrod 5356 |
ER5356 |
SG AlMg5 |
120 |
265 |
26 |
|
＜0.1 |
0.15 |
Mg4.9 |
＜0.2 |
bal. |
|
|
OK Autrod 5183 |
ER5183 |
SG AlMg4.5Mn |
140 |
290 |
25 |
+20 ℃ 30 |
＜0.2 |
0.6 |
Mg4.8 |
＜0.2 |
Bal. |
|
|
***弧焊丝 |
OK Tigrod 1100 |
|
SG Al99.5 |
35 |
75 |
33 |
|
＜0.2 |
0.01 |
0.01 |
0.2 |
＞99.5 |
|
OK Tigrod 4043 |
ER4043 |
SG AlSi5 |
55 |
165 |
18 |
|
5.0 |
0.01 |
0.02 |
0.2 |
bal. |
|
|
OK Tigrod 4047 |
ER4047 |
SG AlSi12 |
80 |
170 |
12 |
|
12.0 |
0.01 |
0.02 |
＜0.2 |
bal. |
|
|
OK Tigrod 5356 |
ER5356 |
SG AlMg5 |
120 |
265 |
26 |
|
＜0.1 |
0.15 |
Mg4.9 |
＜0.2 |
bal. |
|
|
OK Tigrod 5183 |
ER5183 |
SG AlMg4.5Mn |
140 |
290 |
25 |
+20 ℃ 30 |
＜0.2 |
0.6 |
Mg4.8 |
＜0.2 |
Bal. |
|
OK AristoRod新一代无镀层MAG焊丝
铝硅焊丝4043 制冷行业***焊丝
ER4043是含硅5%的铝硅合金焊丝，也称S311，流动性好，抗热裂能力强，但延展性不足。由于含硅量较高，用于高镁合金的焊接时，容易在焊缝中生成脆性Mg2Si,使接头的塑性和耐蚀性降低。此外，焊接表面颜色发暗，阳极化处理后更与母材颜色不同。
用作除铝镁合金以外的铝合金工件和铸件的***弧焊及气焊时的填充材料。常用于6061等6XXX系列铝合金、3XXX系和2XXX系铝合金及铸铝的焊接。广泛用于船舶、机车、化工、食品、运动器材、模具、家具、容器、集装箱。
铝硅焊丝有较强的抗裂性，但塑性较差，所以对焊后需要塑性变形加工的接头来说，应避免选用铝硅焊丝。
化学成份：Si:4.50-6.0 Fe:0.80 Cu:0.30 Mn:0.05 Mg:0.05 Cr:-- Zn:0.10 Ti:0.20 AL:余量;
焊缝机械性能（参考值）：
抗拉强度：120-150MPa
屈服强度：50-65MPa
延伸率：10-18%
导电率：42%IACS
线膨胀系数：22 10-6/K（20-100℃）
熔化温度：575～630℃
化学成分执行标准：GB/T3190-1998
焊丝标准：GB10858-2008 相当于ANSI/AWS A5.10-92