LLDPE(线型低密度聚乙烯#线型高压聚乙烯)/218NJ/沙特sabic
原料描述部分
|
规格级别 |
薄膜级 |
|
该料用途 |
中等承重吹塑膜，与其他树脂混合 |
|
备注说明 |
柔韧，延伸性好，易压制 |
原料技术数据
|
性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
||
|
基本性能 |
熔体流动速率 |
190℃/2.16kg |
ASTM D-1238 |
2.0 |
g/10min |
|
|
密度 |
23℃ |
ASTM D-792 |
0.918 |
g/cm3 |
||
|
物理性能 |
混浊 |
|
ASTM D-1003 |
15 |
% |
|
|
光泽度 |
60℃ |
ASTM D-2457 |
60 |
% |
||
|
机械性能 |
抗穿刺强度 |
|
SABIC |
63 |
J/mm |
|
|
落锤冲击 |
|
ASTM D-1709 |
110 |
g |
||
|
1%割线模量 |
MD |
|
ASTM D-882 |
220 |
MPa |
|
|
TD |
|
ASTM D-882 |
260 |
MPa |
||
|
断裂伸长率 |
MD |
|
ASTM D-882 |
700 |
% |
|
|
TD |
|
ASTM D-882 |
750 |
% |
||
|
断裂拉伸强度 |
MD |
|
ASTM D-882 |
35 |
MPa |
|
|
TD |
|
ASTM D-882 |
29 |
MPa |
||
|
屈服拉伸强度 |
MD |
|
ASTM D-882 |
12 |
MPa |
|
|
TD |
|
ASTM D-882 |
10 |
MPa |
||
|
门氏撕裂强度 |
MD |
|
ASTM D-1922 |
135 |
g |
|
|
TD |
|
ASTM D-1922 |
400 |
g |
||