一种适用于焊接NiCu合金或焊接NiCu合金与钢材的镍铜焊条，可生成耐蚀表面。OK NiCu-7的焊缝金属具有良好的抗裂纹和延展性能，能够满足海水以及氧化/还原性酸环境对抗腐蚀性的严苛要求。OK NiCu-7适用于石油业、***铵工业以及发电厂焊接抗腐蚀蒙乃尔合金。
Typical Tensile Properties
| As welded | |||
| Elongation | Tensile Strength | Yield Strength | 保护气体 |
| 40 % | 640 MPa | 410 MPa | AWS |
夏比V型缺口冲击性能
| As welded | ||
| Impact Value | Testing Temperature | 保护气体 |
| 100 J | 20 °C | AWS |
| 80 J | -196 °C | AWS |
焊缝金属分析
| Mn | ||||||
| Mn | Cu | C | Ti | Si | Ni | Fe |
| 3.0 % | - | - | - | - | - | - |
| Cu | ||||||
| Mn | Cu | C | Ti | Si | Ni | Fe |
| - | 29 % | - | - | - | - | - |
| C | ||||||
| Mn | Cu | C | Ti | Si | Ni | Fe |
| - | - | 0.02 % | - | - | - | - |
| Ti | ||||||
| Mn | Cu | C | Ti | Si | Ni | Fe |
| - | - | - | 0.4 % | - | - | - |
| Si | ||||||
| Mn | Cu | C | Ti | Si | Ni | Fe |
| - | - | - | - | 0.5 % | - | - |
| Ni | ||||||
| Mn | Cu | C | Ti | Si | Ni | Fe |
| - | - | - | - | - | 66 % | - |
| Fe | ||||||
| Mn | Cu | C | Ti | Si | Ni | Fe |
| - | - | - | - | - | - | 1.9 % |
熔敷数据
| Fusion time per electrode at 90% I max | kg weld metal/kg electrodes | Number of electrodes/kg weld metal | 安培 | 熔敷率 | 电压 V | 直径 |
| 45 sec | 0.63 kg | 83 | 50-70 A | 1.0 kg/h | 22 V | 2.5 x 300 mm |
| 52 sec | 0.63 kg | 42 | 70-120 A | 1.6 kg/h | 26 V | 3.2 x 350 mm |
| 54 sec | 0.63 kg | 28 | 120-140 A | 2.4 kg/h | 28 V | 4.0 x 350 mm |