He***y coated general purpose hardfacing electrode for worn parts providing a hardness level of approximately 45 HRC.
焊缝金属分析
Mn | |||
Mn | C | Si | Cr |
2.0 % | - | - | - |
C | |||
Mn | C | Si | Cr |
- | 0.3 % | - | - |
Si | |||
Mn | C | Si | Cr |
- | - | 0.8 % | - |
Cr | |||
Mn | C | Si | Cr |
- | - | - | 1.3 % |
熔敷数据
Fusion time per electrode at 90% I max | kg weld metal/kg electrodes | Number of electrodes/kg weld metal | 安培 | 熔敷率 | 电压 V | 直径 |
94 sec | 0,63 kg | 35,3 | 100-130 A | 1,1 kg/h | 24 V | 3.2 x 450 mm |
105 sec | 0,6 kg | 25 | 130-180 A | 1,4 kg/h | 26 V | 4.0 x 450 mm |
124 sec | 0,64 kg | 15,4 | 180-220 A | 1,9 kg/h | 25 V | 5.0 x 450 mm |