含有2Cr 1Mo的全位置金红石药芯焊丝。设计用于配合Ar/15-25%CO2保护气体使用。
Typical Tensile Properties
| PWHT 690°C 1h | ||
| Elongation | Tensile Strength | Yield Strength |
| 20 % | 710 MPa | 625 MPa |
夏比V型缺口冲击性能
| PWHT 690°C 1h | |
| Impact Value | Testing Temperature |
| 130 J | 20 °C |
| 110 J | 0 °C |
| 65 J | -20 °C |
焊缝金属分析
| Mn | ||||
| Mn | Mo | C | Si | Cr |
| 0.84 % | - | - | - | - |
| Mo | ||||
| Mn | Mo | C | Si | Cr |
| - | 0.94 % | - | - | - |
| C | ||||
| Mn | Mo | C | Si | Cr |
| - | - | 0.06 % | - | - |
| Si | ||||
| Mn | Mo | C | Si | Cr |
| - | - | - | 0.33 % | - |
| Cr | ||||
| Mn | Mo | C | Si | Cr |
| - | - | - | - | 2.26 % |
熔敷数据
| 安培 | 熔敷率 | 电压 V | 直径 | 送丝速度 |
| 150-350 A | 2.1-7.5 kg/h | 23-35 V | 1.2 mm | 5.8-20.7 m/min |