Arcaloy MC316L is a composite metal cored stainless steel wire which has a stainless steel sheath. The addition of molybdenum helps reduce pitting corrosion. As a ***all diameter cored wire it can be used for the welding of thin gauge 316, 316L and sometimes 304 and 304L stainless steels. Its higher deposition rate and less penetration compared to solid wire makes it very suitable for making butt, fillet and lap welds on gauge material. Higher speeds are also possible compared to solid wire. The low spatter and slag-free welds make this electrode ideal for automatic and robotic welding. The pushing technique can be used to further minimize the penetration and oxide film formed on the surface of the weld. Typical applicati*** include automobile catalytic converters, manifolds, mufflers, exhaust systems. For welding in the spray mode of metal transfer, the shielding gas should be argon with 1% or 2% oxygen or carbon dioxide. Pulse welding can also be used to further minimize penetration in thin gauge steels. This metal cored wire can also be used in submerged arc welding. It can be used with OK Flux 10.93.
焊缝金属分析
| 98% Ar / 2% CO2 |
| As Welded |
| 7 FN % |
熔敷数据
| 安培 | 效率 (%) | 熔敷率 | 电压 V | 直径 | 送丝速度 |
| 144 A | 99.3 % | 1.9 kg/h | 16 V | .045 in. | 160 in./min |
| 245 A | 99.3 % | 3.2 kg/h | 25 V | .045 in. | 265 in./min |
| 321 A | 99.4 % | 10 lb/h | 26 V | .045 in. | 370 in./min |
| 390 A | 98.5 % | 13 lb/h | 28 V | .045 in. | 1206 cm/min |
| 441 A | 99.2 % | 16 lb/h | 30 V | .045 in. | 1473 cm/min |
| 212 A | 99.2 % | 3.1 kg/h | 23 V | 1.6 mm | 145 in./min |
| 285 A | 98.8 % | 10.8 lb/h | 23 V | 1.6 mm | 225 in./min |
| 332 A | 98.1 % | 13.7 lb/h | 26 V | 1.6 mm | 300 in./min |
| 420 A | 99.5 % | 18.3 lb/h | 28 V | 1.6 mm | 380 in./min |
| 500 A | 98.9 % | 10.22 kg/h | 31 V | 1.6 mm | 1168 cm/min |