OK Tigrod 13.09是一种0.5Mo合金化镀铜焊丝,适用于诸如压力容器及锅炉内部管道等工作温度***高约500°C相同牌号抗蠕变钢的GTAW焊接。
Typical Tensile Properties
AWS Ar (I1) PWHT 620°C 1h | ||
Elongation | Tensile Strength | Yield Strength |
28 % | 610 MPa | 510 MPa |
AWS Ar (I1) As welded | ||
Elongation | Tensile Strength | Yield Strength |
27 % | 620 MPa | 520 MPa |
EN Ar (I1) PWHT 620°C 1h | ||
Elongation | Tensile Strength | Yield Strength |
31 % | 550 MPa | 450 MPa |
EN Ar (I1) As welded | ||
Elongation | Tensile Strength | Yield Strength |
30 % | 600 MPa | 490 MPa |
夏比V型缺口冲击性能
AWS Ar (I1) PWHT 620°C 1h | |
Impact Value | Testing Temperature |
220 J | -20 °C |
AWS Ar (I1) As welded | |
Impact Value | Testing Temperature |
150 J | -29 °C |
130 J | -46 °C |
EN Ar (I1) PWHT 620°C 1h | |
Impact Value | Testing Temperature |
190 J | 20 °C |
170 J | -20 °C |
EN Ar (I1) As welded | |
Impact Value | Testing Temperature |
180 J | 20 °C |
160 J | -20 °C |
90 J | -40 °C |
25 J | -60 °C |
焊缝金属分析
Mn | |||||
Mn | Mo | C | Si | Ni | Cr |
1.09 % | - | - | - | - | - |
Mo | |||||
Mn | Mo | C | Si | Ni | Cr |
- | 0.45 % | - | - | - | - |
C | |||||
Mn | Mo | C | Si | Ni | Cr |
- | - | 0.094 % | - | - | - |
Si | |||||
Mn | Mo | C | Si | Ni | Cr |
- | - | - | 0.61 % | - | - |
Ni | |||||
Mn | Mo | C | Si | Ni | Cr |
- | - | - | - | 0.05 % | - |
Cr | |||||
Mn | Mo | C | Si | Ni | Cr |
- | - | - | - | - | 0.05 % |