适用于焊接含有5% Mg的铝合金和需要达到较高抗拉强度合金的焊丝。合金化元素Zr在硬化凝固过程中具有优良的抗热裂纹作用。
Typical Tensile Properties
| As welded | ||
| Elongation | Tensile Strength | Yield Strength |
| 30 % | 280 MPa | 130 MPa |
夏比V型缺口冲击性能
| As welded | |
| Impact Value | Testing Temperature |
| 35 J | 20 °C |
焊缝金属分析
| Mn | |||||||||
| Mn | Cu | Zn | Ti | Si | Zr | Mg | Al | Cr | Fe |
| 0.8 % | - | - | - | - | - | - | - | - | - |
| Cu | |||||||||
| Mn | Cu | Zn | Ti | Si | Zr | Mg | Al | Cr | Fe |
| - | 0.01 % | - | - | - | - | - | - | - | - |
| Zn | |||||||||
| Mn | Cu | Zn | Ti | Si | Zr | Mg | Al | Cr | Fe |
| - | - | 0.01 % | - | - | - | - | - | - | - |
| Ti | |||||||||
| Mn | Cu | Zn | Ti | Si | Zr | Mg | Al | Cr | Fe |
| - | - | - | 0.08 % | - | - | - | - | - | - |
| Si | |||||||||
| Mn | Cu | Zn | Ti | Si | Zr | Mg | Al | Cr | Fe |
| - | - | - | - | 0.04 % | - | - | - | - | - |
| Zr | |||||||||
| Mn | Cu | Zn | Ti | Si | Zr | Mg | Al | Cr | Fe |
| - | - | - | - | - | 0.11 % | - | - | - | - |
| Mg | |||||||||
| Mn | Cu | Zn | Ti | Si | Zr | Mg | Al | Cr | Fe |
| - | - | - | - | - | - | 4.7 % | - | - | - |
| Al | |||||||||
| Mn | Cu | Zn | Ti | Si | Zr | Mg | Al | Cr | Fe |
| - | - | - | - | - | - | - | Rem % | - | - |
| Cr | |||||||||
| Mn | Cu | Zn | Ti | Si | Zr | Mg | Al | Cr | Fe |
| - | - | - | - | - | - | - | - | 0.08 % | - |
| Fe | |||||||||
| Mn | Cu | Zn | Ti | Si | Zr | Mg | Al | Cr | Fe |
| - | - | - | - | - | - | - | - | - | 0.12 % |