适用于无氧纯铜和低合金铜GMA焊接的实芯铜焊丝。OK Autrod 19.12含有锡的合金化元素，具有良好的流送性。OK Autrod 19.12通常使用纯Ar作为保护气体进行焊接。
Typical Tensile Properties
| As welded | ||
| Elongation | Tensile Strength | Yield Strength |
| 30 % | 220 MPa | 75 MPa |
焊缝金属分析
| Mn | |||
| Mn | Cu | Si | Fe |
| 0.2 % | - | - | - |
| Cu | |||
| Mn | Cu | Si | Fe |
| - | Bal % | - | - |
| Si | |||
| Mn | Cu | Si | Fe |
| - | - | 0.2 % | - |
| Fe | |||
| Mn | Cu | Si | Fe |
| - | - | - | 0.05 % |
熔敷数据
| 安培 | 电压 V | 直径 | 送丝速度 |
| 60-165 A | 13-17.5 V | 0.8 mm | 4-13 m/min |
| 80-210 A | 12.5-18 V | 1.0 mm | 4-12 m/min |
| 150-320 A | 16-29 V | 1.2 mm | 5-11.5 m/min |