PA6 德国巴斯夫 PA6 Ultramid BASF
B 24 N 03,B 24 NFD 05,B 24 NSD 05,B 27 03,B 27 15,B 27 E 01,B 27 E,B 27 SD 02,B 27 SD 05,B 29 HM 01,B 32 01,B 32,
B 33 01,B 33 L 01,B 33 L,B 33LN 01,B 35EG3,B 35G3 BK00564,B 36 01,B 36 LN 01,B 36 LN,B 36,B 3EG3 BK00564,B 3EG3,
B 3EG5,B 3EG6 BK00564,B 3EG6,B 3EG7 BK00564,B 3EG7,B 3G8 BK00564,B 3GK24,B 3GM35 BK30564,B 3GM35 BK60564,
B 3GM35 BKQ642 23220,B 3GM35 BKQ649 23220,B 3GM35 Ebony23227,B 3GM35 Q611,B 3GM35 Q643,B 3K BK00464,B 3K,
B 3L BK00464,B 3L,B 3M6 BK30564,B 3M6 BK60564,B 3M6,B 3S BK00464,B 3S HP,B 3S Q661,B 3S,B 3UG4,B 3WG10 BK564,
B 3WG5 BK00564,B 3WG5,B 3WG6 BK00564 BGVW,B 3WG6 BK00564,B 3WG6 CR BK23210,B 3WG6 GP bk 23210,B 3WG7 BK00564,B
3WG7,B 3WGM24 BK23228,B 3WGM24 BK30564,B 3WGM24 HP BK23210,B 3WGM24 HPX BK23210,B 3Z BK30464,B 3ZG3 BK30564,
B 3ZG3,B 3ZG6 BK30564, B 3ZG7 OSI BK23273,B 3ZG8 BK20560,B 3ZG8 sw 20560,B 40 01,B 40 L 01,B 40 L,B 40 LN,B 40,B 40LN 01,
B 50L 01,B G40GM45 HS BK130,B G50XFI,B U50I BK-106,B U50I,8202 HS BK-102,8202 HS,8202 L-Intermediate,8202,8202C HS BK-102,
8202C HS,8202C,8202CQ,8231G HS BK-102,8231G HS BK-106,8231G HS,8232G HS FR BK-102,8232G HS FR,8233G HS BK-102,8233G HS BK-106,
8233G HS,8234G HS BK-102,8234G HS,8235G HS BK-102,8253 HS BK-102,8253 HS,8253,8254 HS BK-102,8255 HS,8260 HS BK-102,8260,
8262G HS BK-102,8267G HS BK-102,8267G HS BK-106,8267G HS BK-106A,8270 HS BK-102,8270 HS,8272G HS BK-102,8281 HS GP,8281 HS,
8333G HI HS BK-102,8333G HI HS BK-106,8333G HI,8350 HS BK-102,8350 HS,TG3S,TG7S BK-102,TG7S,TG3S BK-104,SEG7,SEG8 BK-126,
SEGM35 H1 BK-126,SEGM35 H1 BK6259,HPN 9233G HS BK-102,HPN 9350 HS,HPN 9362,HFX 33,HFX 35,HFX 37,HMG13 HS BK-102,8351 HS BK-102,8351 HS BK-106
物理性能 |
额定值
|
单位制
|
测试方法
|
比重
|
1.13
|
g/cm³
|
ASTM D792 |
收缩率 - 流动 (3.18 mm)
|
2.0
|
%
|
|
吸水率
|
ASTM D570 | ||
24 hr
|
1.3
|
%
|
|
饱和
|
9.5
|
%
|
|
平衡, 50% RH
|
2.7
|
%
|
|
硬度 |
额定值
|
单位制
|
测试方法
|
洛氏硬度 (R 计秤)
|
116
|
|
ASTM D785 |
机械性能 |
额定值
|
单位制
|
测试方法
|
抗张强度
|
ASTM D638 | ||
屈服, -40°C
|
114
|
MPa
|
|
屈服, 23°C
|
72.0
|
MPa
|
|
屈服, 121°C
|
20.0
|
MPa
|
|
伸长率 (断裂, 23°C)
|
> 100
|
%
|
ASTM D638 |
弯曲模量
|
ASTM D790 | ||
-40°C
|
2760
|
MPa
|
|
23°C
|
2690
|
MPa
|
|
65°C
|
530
|
MPa
|
|
90°C
|
360
|
MPa
|
|
121°C
|
300
|
MPa
|
|
弯曲强度
|
ASTM D790 | ||
-40°C
|
154
|
MPa
|
|
23°C
|
100
|
MPa
|
|
65°C
|
30.0
|
MPa
|
|
90°C
|
20.0
|
MPa
|
|
121°C
|
15.0
|
MPa
|
|
冲击性能 |
额定值
|
单位制
|
测试方法
|
悬壁梁缺口冲击强度
|
ASTM D256 | ||
-40°C
|
45
|
J/m
|
|
23°C
|
55
|
J/m
|
|
Drop Impact Resistance (23°C)
|
67.8
|
J
|
内部方法 |
热性能 |
额定值
|
单位制
|
测试方法
|
热变形温度 (1.8 MPa, 未退火)
|
60.0
|
°C
|
ASTM D648 |
熔融峰值温度
|
220
|
°C
|
ASTM D3418 |
线形膨胀系数 - 流动
|
0.000074
|
cm/cm/°C
|